Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 45.0 min @Temperature 130 °C |
0.750 hour @Temperature 266 °F |
Oven |
Permabond ES550 Epoxy Resin PERMABOND ES550 is a single-part epoxy paste which is slump-resistant (does not flow) during cure. The adhesive is toughened for maximum impact resistance, along with excellent peel and shear streng.. |
|||
Cure Time | 45.0 min @Temperature 150 °C |
0.750 hour @Temperature 302 °F |
|
Permabond ES558 Epoxy Resin PERMABOND ES558 is a single-part epoxy paste which flows like solder when heated during curing. The adhesive is toughened for maximum impact resistance, along with excellent peel and shear strength... |
|||
Cure Time | 45.0 min @Temperature 120 °C |
0.750 hour @Temperature 248 °F |
Oven |
Permabond ES562 Epoxy Resin PERMABOND® ES562 is a single-part epoxy adhesive which flows like solder when heated during curing. The adhesive has excellent adhesion to metal surfaces and composites. The high bond strength of t.. |
|||
Cure Time | 45.0 - 60.0 min @Temperature 60.0 °C |
0.750 - 1.00 hour @Temperature 140 °F |
Full cure in 45 to 60 mins at 140°F. |
Fibre Glast 1101 High-Strength General Purpose Epoxy Adhesive Description:#1101 is a light grayish-tan two part epoxy adhesive that was developed especially for difficult bonding problems involving similar or dissimilar materials. #1101 provides excellent adhe.. |
|||
Cure Time | 45.0 - 60.0 min | 0.750 - 1.00 hour | Functional cure |
ITW Devcon Plastic Welderâ„¢ Methacrylate Adhesive, Straw, White, Black Information provided by ITW Devcon |
|||
Cure Time | 45.0 min | 0.750 hour | Tack-free |
Momentive Performance Materials RTV5243 Neutral Cure, One Component RTV Adhesive Sealant RTV5240 series sealants are alkoxy neutral cure, one-component, ready to use, electronic grade silicone adhesive sealants exhibiting high strength that will maintain a strong bond even when exposed .. |
|||
Cure Time | 45.0 min @Temperature 152 °C |
0.750 hour @Temperature 305 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 5 PHR Di-Cup 40C MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 45.0 min @Temperature 152 °C |
0.750 hour @Temperature 305 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 8 PHR Di-Cup 40C MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 45.0 min @Temperature 125 °C |
0.750 hour @Temperature 257 °F |
|
Dow Corning SE 4445 CV KIT Two-part, grey, 1:1, addition cure gel, good thermal conductivity, controlled volatility, UL V-0.Information provided by Dow Corning |
|||
Cure Time | 45.0 min @Temperature 25.0 °C |
0.750 hour @Temperature 77.0 °F |
Full Chemical |
Chesterton ARC 5ES Rapid Repair Stick Description: ARC 5ES is specifically formulated for quick reliable repairs. Its “stick” design combines the performance of a two component system with the convenience of a single component. The AR.. |
|||
Cure Time | >= 45.0 min | >= 0.750 hour | Tack Free Time |
ACC EP AEP EPI Engineered Polymers EP AEP is a new generation of Internetwork Polymers of polyurea and Epoxy, “Powered by Reactamine® Technology”. EP AEP was developed for a colorfast floor for both residential and industrial appl.. |
|||
Cure Time | 45.0 - 60.0 min | 0.750 - 1.00 hour | Tack Free Time, catalyzed with QM CAT RED 3 |
ACC QM 107 QSI Quantum Silicones 7 Durometer Condensation Cure Moldmaking Material QM 107 is a two component, room temperature condensation cure silicone material. The cured rubber is very soft, has excellent mechanical properties and good shelf-life stability. This material is us.. |
|||
Cure Time | 45.0 - 60.0 min | 0.750 - 1.00 hour | Tack Free Time, catalyzed with QM CAT RED 3 |
ACC QM 122 QSI Quantum Silicones 22 Durometer Condensation Cured Moldmaking Material QM 122 is a two-component, room temperature condensation cure silicone material. The cured rubber is flexible with excellent mechanical and physical properties in addition to good shelf-life stabili.. |
|||
Cure Time | 45.0 - 60.0 min | 0.750 - 1.00 hour | Tack Free Time, catalyzed with QM CAT RED 3 |
ACC QM128 QSI Quantum Silicones 28 Durometer Condensation Cured Moldmaking Material QM 128 is a two-component, room temperature condensation cure silicone material. The cured rubber has excellent mechanical properties and shelf-life stability. This material is an excellent choice f.. |
|||
Cure Time | 45.0 - 75.0 min @Temperature 24.0 °C |
0.750 - 1.25 hour @Temperature 75.2 °F |
|
BCC Products BC 4578 Polyester Model Board Filler BC 4578 is a quick setting easy to use filler paste which is designed specifically for repair to Model Board MB 2001. Its lightweight characteristic and tack free cure makes for ease of finishing wi.. |
|||
Cure Time | 45.0 min @Temperature 249 °C |
0.750 hour @Temperature 480 °F |
|
Aremco Corr-Paint™ CP4010S High Temperature Protective Coating Silicone-Polyester |
|||
Cure Time | 45.0 min @Temperature 249 °C |
0.750 hour @Temperature 480 °F |
|
Aremco Corr-Paint™ CP4010-S1 High Temperature Protective Coating, Silicone |
|||
Cure Time | 45.0 min @Temperature 232 °C |
0.750 hour @Temperature 450 °F |
Adequate ventilation is required when curing these products. Outgassing will occur above 300°F and cease after 750°F. An additional 30 minutes is required at the highest service temperature if service temperature is below 750°F. |
Aremco Corr-Paint™ CP4050 High Temperature Protective Coating Silicone Low viscosity, green coating for power resistors to 1100°F (593°C) |
|||
Cure Time | 45.0 min @Temperature 249 °C |
0.750 hour @Temperature 480 °F |
|
Aremco Corr-Paint™ CP4060 High Temperature Protective Coating Silicone, Aluminum Filled This silicone-based, heat resistant coatings are formulated using a state-of-the-art, VOC-compliant, water-dispersible silicone resin. CP4000 adheres to metals, ceramics, refractories, and quartz, a.. |
|||
Cure Time | 45.0 min @Temperature 249 °C |
0.750 hour @Temperature 480 °F |
|
Aremco Corr-Paint™ CP4080-S High Temperature Protective Coating, Silicone-Polyester |
|||
Cure Time | 45.0 min @Temperature 249 °C |
0.750 hour @Temperature 480 °F |
|
Aremco Corr-Paint™ CP4095-S High Temperature Protective Coating, Silicone-Polyester |
|||
Cure Time | 45.0 min @Temperature 249 °C |
0.750 hour @Temperature 480 °F |
|
Aremco HiE-Coat™ 840-MS High Emissivity Coating, Silicone-Ceramic Filled Silicone-ceramic, black pigmented single component coating for aluminum, brass, copper, and carbon and stainless steel to 1100 °F (593 °C). |
|||
Cure Time | 45.0 min @Temperature 249 °C |
0.750 hour @Temperature 480 °F |
preceeded by 1 hour air set |
Aremco HiE-Coat™ 840-MS High Emissivity Silicone-Ceramic Coating 840-C is a silicone-ceramic, black-pigmented coating for aluminum, brass, copper, and carbon and stainless steels to 1100 ºF (593 ºC).The HiE-Coat™ line of high emissivity coatings are black-body.. |
|||
Cure Time | 45.0 min @Temperature 232 °C |
0.750 hour @Temperature 450 °F |
Adequate ventilation is required when curing these products. Outgassing will occur above 300°F and cease after 750°F. An additional 30 minutes is required at the highest service temperature if service temperature is below 750°F. |
Aremco Aremco-Seal™ 4030 High Temperature Specialty Coatings Silicone, Ceramic Filled Translucent-white, low-viscosity sealer for porous materials to 900°F (482°C) |
|||
Cure Time | 45.0 min @Temperature 249 °C |
0.750 hour @Temperature 480 °F |
|
Aremco Corr-Paint™ CP4000-S High Temperature Protective Coating Silicone-Polyester |
|||
Cure Time | 45.0 min @Temperature 249 °C |
0.750 hour @Temperature 480 °F |
|
Aremco Corr-Paint™ CP4020 High Temperature Protective Coating Silicone, Aluminum Filled This silicone-based, heat resistant coatings are formulated using a state-of-the-art, VOC-compliant, water-dispersible silicone resin. CP4010 adheres to metals, ceramics, refractories, and quartz, a.. |
|||
Cure Time | 45.0 min @Temperature 232 °C |
0.750 hour @Temperature 450 °F |
Adequate ventilation is required when curing these products. Outgassing will occur above 300°F and cease after 750°F. An additional 30 minutes is required at the highest service temperature if service temperature is below 750°F. |
Aremco Corr-Paint™ CP4040 High Temperature Protective Coating Silicone Low viscosity, white coating for motor windings to 1100°F (593°C) |
|||
Cure Time | 45.0 min @Temperature 249 °C |
0.750 hour @Temperature 480 °F |
|
Aremco Corr-Paint™ CP4050-S1 High Temperature Protective Coating, Silicone |
|||
Cure Time | 45.0 min @Temperature 249 °C |
0.750 hour @Temperature 480 °F |
|
Aremco Corr-Paint™ CP4095 High Temperature Protective Coating Silicone, Aluminum Filled This silicone-based, heat resistant coatings are formulated using a state-of-the-art, VOC-compliant, water-dispersible silicone resin. CP4000 adheres to metals, ceramics, refractories, and quartz, a.. |