- Polymer Property : Maximum Service Temperature, Air = 293 °F
Polymer Property : Maximum Service Temperature, Air = 293 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 145 °C | 293 °F | Continuous; FRISETTA Test Method |
| Nilit FRIANYL B63 TF-GV 1520 Nylon 6 for injection molding, 15% PTFE lubricated, 20% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | <20000 hours; IEC 60216-P1 |
| Hexion Bakelite™ PF 2400 Phenolic Formaldehyde Resin, High Surface Quality, Dishwasher Proof, UL Listed
(disc Phenolic molding compound, inorganically/organically filled, average heat resistance, increased dimensional stability, dish washer proof, UL listed molding compound 1.5 mm/V-0 (ALL).Application area.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Industrial Laminates/Norplex NP313 Cotton Fabric Description: Canvas phenolic laminate with molybdenum disulfide lubricant. Mechanical properties slightly lower than NP310.Thickness Tested: 0.062", 0.125" & 0.500" |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Industrial Laminates/Norplex NP315 Cotton Fabric Description: Canvas phenolic laminate with graphite added as a solid lubricant. This material has improved wear properties under certain conditions. Material is conductive to electricity and should .. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| LATI Laramid G/35 PPA, 35% Glass Fiber Reinforced Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; .. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | Short peaks operation |
| Polyram PlusTek PD305G6 Nylon 12 for Injection Molding, 30% Glass-fiber Reinforced 30% Glass-fiber reinforced Nylon 12 for injection molding applications.Information provided by Polyram. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond 716C01 Medium Viscosity Epoxy Adhesive TRA-BOND 716C01 is a medium viscosity epoxy resin system specifically developed for bonding and coating applications. This two-part amber adhesive is easily mixed, used and cured at room temperature.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond FDA12 Food and Drug Application Epoxy Adhesive TRA-BOND FDA12 is a medium viscosity epoxy resin system specifically developed for bonding and coating applications in accordance with Title 21, U.S. Code of Federal Regulations, Food and Drug Admin.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond FDA16 Food and Drug Application Epoxy Adhesive TRA-BOND FDA-16 EPOXY ADHESIVE is a medium viscosity epoxy resin system specifically developed for medical device applications. It has been tested in accordance with USP biological reactivity tests,.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond FDA22 Food and Drug Application Epoxy Adhesive TRA-BOND FDA-22 is a high viscosity epoxy resin system specifically developed for bonding and coating applications in accordance with Title 21, U.S. Code of Federal Regulations, Food and Drug Admini.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond FDA23 Food and Drug Application Epoxy Adhesive TRA-BOND FDA-23 is a high viscosity epoxy resin system specifically developed for bonding and coating applications in accordance with Title 21, U.S. Code of Federal Regulations, Food and Drug Admini.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond FDA2YL02 Food and Drug Application Epoxy Adhesive TRA-BOND FDA-2 YL02 is a medium viscosity epoxy resin system specifically developed for adhesive and coating applications in accordance with Title 21, U.S. Code of Federal Regulations, Food and Drug.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Cast 3113 General Purpose Epoxy Casting Compound TRA-CAST 3113 is a low viscosity two-part formulation recommended for general purpose electrical potting and encapsulating applications where the combination of good mechanical thermal and electrica.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Cast 3135 Low Viscosity Encapsulant TRA-CAST 3135 is a low viscosity adhesive developed for demanding electronic underfill and encapsulant adhesive applications. This solvent free material is readily mixed, and cured at room temperatu.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond RO7 Radio Opaque Epoxy Adhesive TRA-BOND RO-7 is a high viscosity epoxy resin system specifically developed for adhesive and coating applications where radio opacity is required. It can be used as an X-ray marker on in-vitro medic.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | few hours; VDE 0304/P2-1, IEC 216 |
| EPICHEM Epilon G2-PC 10% GF Polycarbonate, 10% Glass Fiber Characteristics: 10% glass fibre filled, good mechanical properties |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | few hours; VDE 0304/P2-1, IEC 216 |
| EPICHEM Epilon G4-PC 20% GF Polycarbonate, 20% Glass Fiber Characteristics: 20% glass fibre filled, excellent mechanical properties |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | 5000 h; VDE 0304/P2-1, IEC 216 |
| EPICHEM Epilon PC GF 10 V0 Polycarbonate, 10% Glass Fiber Characteristics: self-extinguishing V0 at 1,6 mm, 10% glass fibre filled |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| BASF Ultramid® B3WG7 BK 00564 35% Glass Filled PA6 (Conditioned) Description: 35% glass-fiber reinforced and heat aging resistant injection-molding grade, e.g. for automotive manifolds and pedals.Information provided by BASF |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Atom Adhesives AA-BOND FDA2T Epoxy Adhesive AA-BOND FDA2T is a thixotropic epoxy resin system specifically developed for medical device applications. It has been tested in accordance with USP biological reactivity tests, in vivo and received .. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| BASF Ultramid® A3WG3 15% Glass Filled PA66 (Dry) Description: 15% Glass-fiber reinforced and heat aging resistant injection-molding grade for machine elements and housings of medium stiffness. For electric insulating parts, preference should be gi.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20,000 hr |
| BASF Ultramid® A3WG5 25% Glass Filled PA66 (Conditioned) Ultramid A3WG5 is a 25% glass fiber reinforced and heat resistance injection molding PA66 grade. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| BASF Ultramid® A3WG6 BK 00564 30% Glass Filled PA66 (Conditioned) Description: 30% glass-fiber reinforced and heat aging resistant injection-molding grade for machine elements and housings of high stiffness and dimensional stability such as lamp socket housings, f.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20,000 hr |
| BASF Ultramid® B3WG6 BK00564 30% Glass Filled PA6 (Conditioned) Ultramid B3WG6 BK00564 is a 30% glass fiber reinforced, pigmented black, heat stabilized injection molding PA6 grade. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| BASF Ultramid® B3WG7 BK 00564 30% Glass Filled PA6 (Dry) Description: 35% glass-fiber reinforced and heat aging resistant injection-molding grade, e.g. for automotive manifolds and pedals.Information provided by BASF |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| BASF Ultramid® B3WG10 BK 00564 50% Glass Filled PA6 (Conditioned) Description: 50% glass-fiber reinforced and heat aging resistant injection-molding grade for technical parts with very high stiffness.Information provided by BASF |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| BASF Ultramid® B3WG5 BK 00564 25% Glass Filled PA6 (Conditioned) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20,000 hr |
| BASF Ultramid® B3WG6 30% Glass Filled PA6 (Conditioned) Ultramid B3WG6 is a 30% glass fiber reinforced, heat stabilized injection molding PA6 grade. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20,000 hr |
| BASF Ultramid® B3WG6 30% Glass Filled PA6 (Dry) Ultramid B3WG6 is a 30% glass fiber reinforced, heat stabilized injection molding PA6 grade. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20,000 hr |
| BASF Ultramid® B3WG6 BK00564 30% Glass Filled PA6 (Dry) Ultramid B3WG6 BK00564 is a 30% glass fiber reinforced, pigmented black, heat stabilized injection molding PA6 grade. |
|||