BASF Ultramid® B3WG7 BK 00564 35% Glass Filled PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3WG7 BK 00564 35% Glass Filled PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: 35% glass-fiber reinforced and heat aging resistant injection-molding grade, e.g. for automotive manifolds and pedals.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Water Absorption | 5.9 - 6.5 % | 5.9 - 6.5 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 1.8 - 2.2 % | 1.8 - 2.2 % | 23°C; 50% RH; ISO 62 |
| Viscosity Measurement | 140 | 140 | ISO 307 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | restricted |
| Melt Flow | 66.45 g/10 min @Load 5.00 kg, Temperature 275 °C |
66.45 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 130 MPa | 18900 psi | 50 mm/min; ISO 527-1/-2 |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min; ISO 527-1/-2 |
| Modulus of Elasticity | 7.20 GPa | 1040 ksi | ISO 527-1/-2 |
| Flexural Strength | 200 MPa | 29000 psi | at max force; ISO 178 |
| Flexural Modulus | 6.30 GPa | 914 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 27.0 kJ/m² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Charpy Impact Unnotched | 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 3.30 J/cm² @Temperature 23.0 °C |
15.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Tensile Creep Modulus, 1000 hours | 3300 MPa @Strain <=0.500 % |
479000 psi @Strain <=0.500 % |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | |
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | DIN 53765 |
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| 175 °C | 347 °F | for 50% loss of tensile strength after 5000hr | |
| 200 °C | 392 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 6.2 @Frequency 1.00 Hz |
6.2 @Frequency 1.00 Hz |
IEC 60250 |
| Dissipation Factor | 0.19 @Frequency 1.00e+6 Hz |
0.19 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Test solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK 00564 | |
| Commercial Status | Europe |
Users viewing this material also viewed the following:
- Radici Radilon® CA HS (cond.) Nylon 66/6
- Polymer Resources PCSF-FR G30 Polycarbonate, 30% Glass Reinforced Structural Foam Grade
- LG Chemical LUPOY HP5004A PC/ABS
- Lubrizol Advanced Materials Pearlstick® 45-80/16 Polycaprolactone based TPU
- Spartech Free Flow PVC and Alloy Products for Footwear
- SABIC Innovative Plastics LNP Thermocomp EF008E PEI (Asia Pacific)
- Asahi Kasei Leona® 1402F Nylon 66
- ExxonMobil Escorene® LD 728.61 Molding, extrusion and compounding resin
Copyright © lookpolymers.com All Rights Reserved