Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 9.00 - 140 µm/m-°C @Temperature >=143 °C |
5.00 - 77.8 µin/in-°F @Temperature >=289 °F |
Average value: 94.8 µm/m-°C Grade Count:2 |
Overview of materials for Polyetheretherketone, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PTFE Filled". Each property range of values reported is minimum and maximum values.. |
|||
CTE, linear | 120 - 140 µm/m-°C @Temperature 20.0 °C |
66.7 - 77.8 µin/in-°F @Temperature 68.0 °F |
ASTM E831 |
Polimersan Plastics POLITEF® (PTFE) POLITEF (PTFE) was invented in 1938. It is the most preferable and known fluoropolymer among fluorine polymers. It has superior properties that none of the other industrial plastics have because of .. |
|||
CTE, linear | 100 - 140 µm/m-°C @Temperature 20.0 °C |
55.6 - 77.8 µin/in-°F @Temperature 68.0 °F |
ASTM E831 |
Polimersan Plastics POLITEF® (PTFE) with 15% Glass As a result of Filled-In POLITEF® alloys, apart from all of its superior properties, POLITEF®, according to its usage areas has gained additional properties as described below:Electrical Conductiv.. |
|||
CTE, linear | 120 - 140 µm/m-°C @Temperature 20.0 °C |
66.7 - 77.8 µin/in-°F @Temperature 68.0 °F |
ASTM E831 |
Polimersan Plastics POLITEF® (PTFE) POLITEF (PTFE) was invented in 1938. It is the most preferable and known fluoropolymer among fluorine polymers. It has superior properties that none of the other industrial plastics have because of .. |
|||
CTE, linear | 100 - 140 µm/m-°C @Temperature 20.0 °C |
55.6 - 77.8 µin/in-°F @Temperature 68.0 °F |
ASTM E831 |
Polimersan Plastics POLITEF® (PTFE) with 15% Glass As a result of Filled-In POLITEF® alloys, apart from all of its superior properties, POLITEF®, according to its usage areas has gained additional properties as described below:Electrical Conductiv.. |
|||
CTE, linear | 50.0 - 140 µm/m-°C | 27.8 - 77.8 µin/in-°F | Average value: 71.1 µm/m-°C Grade Count:25 |
Overview of materials for PVC, High Impact This property data is a summary of similar materials in the MatWeb database for the category "PVC, High Impact". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
CTE, linear | 18.0 - 140 µm/m-°C | 10.0 - 77.8 µin/in-°F | Average value: 63.7 µm/m-°C Grade Count:163 |
Overview of materials for PVC, Rigid Grade This property data is a summary of similar materials in the MatWeb database for the category "PVC, Rigid Grade". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
CTE, linear | 54.0 - 140 µm/m-°C | 30.0 - 77.8 µin/in-°F | Average value: 103 µm/m-°C Grade Count:4 |
Overview of materials for Polypropylene, Stainless Fiber, EMI This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Stainless Fiber, EMI". Each property range of values reported is minimum and maximum valu.. |
|||
CTE, linear | 120 - 140 µm/m-°C @Temperature 20.0 °C |
66.7 - 77.8 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Solvay Specialty Polymers Solef® 3108/0903 Anti-static PVDF Compound
(discontinued **) Key features of this grade: Anti-static, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crystall.. |
|||
CTE, linear | 120 - 140 µm/m-°C @Temperature 20.0 °C |
66.7 - 77.8 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Solvay Specialty Polymers Solef® 3208/0150 Anti-friction PVDF Compound
(discontinued **) Key features of this grade: Anti-friction, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crysta.. |
|||
CTE, linear | 80.0 - 140 µm/m-°C @Temperature 20.0 °C |
44.4 - 77.8 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Solvay Specialty Polymers Hylar® 460 PVDF Polyvinylidene Fluoride
(discontinued **) Data provided by the manufacturer.Hylar® polymers have the characteristic stability of fluoropolymers combined with a unique polarity that influences its solubility and electrical properties. In a.. |
|||
CTE, linear | 90.0 - 140 µm/m-°C @Temperature 30.0 - 300 °C |
50.0 - 77.8 µin/in-°F @Temperature 86.0 - 572 °F |
Average value: 113 µm/m-°C Grade Count:2 |
Overview of materials for Polytetrafluoroethylene (PTFE), Conductive Carbon Filled This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Conductive Carbon Filled". Each property range of values reported is min.. |
|||
CTE, linear | 120 - 140 µm/m-°C | 66.7 - 77.8 µin/in-°F | Average value: 126 µm/m-°C Grade Count:16 |
Overview of materials for Polyperfluoroalkoxyethylene (PFA), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyperfluoroalkoxyethylene, Molded/Extruded". Each property range of values reported is minimum and max.. |
|||
CTE, linear | 60.0 - 140 µm/m-°C | 33.3 - 77.8 µin/in-°F | Average value: 97.5 µm/m-°C Grade Count:4 |
Overview of materials for Nylon 12, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap.. |
|||
CTE, linear | 125 - 140 µm/m-°C @Temperature 23.0 - 100 °C |
69.4 - 77.8 µin/in-°F @Temperature 73.4 - 212 °F |
ASTM D696 |
Manifattura Cattaneo PVDF Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
CTE, linear | 110 - 140 µm/m-°C | 61.1 - 77.8 µin/in-°F | |
Master Bond MasterSil 156 Two Part, Low Viscosity Silicone Description: Master Bond MasterSil 156 is a two component, lower viscosity silicone system for high performance potting, encapsulation and sealing. MasterSil 156 combines high temperature resistance.. |
|||
CTE, linear | 120 - 140 µm/m-°C @Temperature 20.0 °C |
66.7 - 77.8 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Zeus PFA Tubing PFA, or perfluoroalkoxy, is well recognized for its ability to maintain mechanical integrity in extreme temperatures even when exposed to caustic chemicals. PFA comes in high purity versions that ar.. |
|||
CTE, linear | 120 - 140 µm/m-°C @Temperature 20.0 °C |
66.7 - 77.8 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Solvay Specialty Polymers Solef® 1008 PVDF Homopolymer
(discontinued **) Key features of this grade: Low Viscosity, All Purpose, Injection, Virgin. Recommended processing is injection. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVDF .. |
|||
CTE, linear | 120 - 140 µm/m-°C @Temperature 20.0 °C |
66.7 - 77.8 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer
(discontinued **) Key features of this grade: Mean Viscosity, All Purpose, Injection/Extrusion, Virgin. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SO.. |
|||
CTE, linear | 120 - 140 µm/m-°C @Temperature 20.0 °C |
66.7 - 77.8 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Solvay Specialty Polymers Solef® 1010 PVDF Homopolymer
(discontinued **) Key features of this grade: Med Viscosity, All Purpose, Extrusion, Virgin. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVDF .. |
|||
CTE, linear | 120 - 140 µm/m-°C @Temperature 20.0 °C |
66.7 - 77.8 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Solvay Specialty Polymers Solef® 1012 PVDF Homopolymer
(discontinued **) Key features of this grade: High Viscosity, Virgin. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-c.. |
|||
CTE, linear | 70.0 - 140 µm/m-°C | 38.9 - 77.8 µin/in-°F | Average value: 119 µm/m-°C Grade Count:29 |
Overview of materials for Acetal Copolymer, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Impact Modified". Each property range of values reported is minimum and maximum values.. |
|||
CTE, linear | 30.0 - 140 µm/m-°C | 16.7 - 77.8 µin/in-°F | Average value: 63.7 µm/m-°C Grade Count:20 |
Overview of materials for Polypropylene, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |
|||
CTE, linear | 140 - 140 µm/m-°C @Temperature 60.0 - 138 °C |
77.8 - 77.8 µin/in-°F @Temperature 140 - 280 °F |
Average value: 140 µm/m-°C Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Bead Filled". Each property range of values reported is minimum .. |