Polymer Property : CTE, linear = 45.0 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature -40.0 - 149 °C |
25.0 µin/in-°F @Temperature -40.0 - 300 °F |
ASTM E831 |
| Quadrant EPP Techtron® PSGF PPS - Compression Molded 40% Glass Reinforced Polyphenylene Sulfide (ASTM Product Data Sheet) |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | Below glass transition temp; ASTM D696 |
| Performance Polymers IPS II PPL-C4219 PEKK (Polyetherketoneketone) Linear Wear Grade Black pellets; Carbon fiber/PTFE/Graphite compoundInformation provided by Infinite Polymer System II. |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | |
| Permabond ES550 Epoxy Resin PERMABOND ES550 is a single-part epoxy paste which is slump-resistant (does not flow) during cure. The adhesive is toughened for maximum impact resistance, along with excellent peel and shear streng.. |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | |
| Permabond ES562 Epoxy Resin PERMABOND® ES562 is a single-part epoxy adhesive which flows like solder when heated during curing. The adhesive has excellent adhesion to metal surfaces and composites. The high bond strength of t.. |
|||
| CTE, linear | 45.0 - 90.0 µm/m-°C | 25.0 - 50.0 µin/in-°F | Average value: 63.7 µm/m-°C Grade Count:46 |
| Overview of materials for PVC, Extruded This property data is a summary of similar materials in the MatWeb database for the category "PVC, Extruded". Each property range of values reported is minimum and maximum values of appropriate MatW.. |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | DIN 53752 |
| Lehmann & Voss LUVOCOM® 50/CF/7/GS/10/TF/5/EM/BK Polycarbonate, with carbon fiber, glass flakes and PTFE, easy flowing Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
| CTE, linear | 45.0 - 65.0 µm/m-°C @Temperature 20.0 °C |
25.0 - 36.1 µin/in-°F @Temperature 68.0 °F |
|
| Hybrid Plastics NanoBondâ„¢ UV Curable Adhesive Generally used for dental and optical applications.Information provided by Hybrid Plastics |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | |
| Lord Adhesives Circalokâ„¢ 6031 A/B Epoxy Encapsulant Circalokâ„¢ 6031 A/B is a two-part epoxy potting compound with excellent electrical properties at elevated temperatures. Good arc-track resistance under high voltage loading and other dielectric .. |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | Below Tg; TMA |
| Lord Adhesives Circalokâ„¢ EP-937 Epoxy Board Level Encapsulant LORD Thermosetâ„¢ EP-937 encapsulant is a black, one-component epoxy specifically designed to meet the needs of coating semiconductor devices on printed circuit boards.All information provided by.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 100 °C |
25.0 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| LyondellBasell Hifaxâ„¢ CB251 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CB251 medium melt flow, 1,200 MPa flexural modulus, low CLTE, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of impact resis.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 23.9 - 260 °C |
25.0 µin/in-°F @Temperature 75.0 - 500 °F |
ASTM E831 |
| Saint-Gobain Meldin® 7021 Isostatically Molded Graphite Filled Polyimide Melidin® 7021 is a self-lubricating thermosetting polyimide that contains 15% graphite filler. Melidin® 7021 has a low coefficient of friction and high heat resistance, and is best for high t.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Teijin Multilon DN-3510F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 10 % filler. Improved stiffness and high fluidity realizes a thin wall.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 100 °C |
25.0 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| A. Schulman POLYTROPE™ TPP 608 Olefinic Elastomer DescriptionPolytrope TPP 608 is an olefinic elastomer exhibiting low thermal expansion, low heat sag and high DOI on painted parts. ApplicationTPP 608 is designed specifically for automotive fascia.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
|
| Toyobo ECOVYLOPET® EMC2301E PET Bottle Recycling Grade, 15% Filler Reinforced Features: PET Bottle Recycling Grade, 15% Filler Reinforced, Modified TypeApplications: Automobile engine head coversHot platesVending machine partsUmbrella ribsInformation provided by Toyobo. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 100 °C |
25.0 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| A. Schulman POLYTROPE™ TPP 608 Olefinic Elastomer DescriptionPolytrope TPP 608 is an olefinic elastomer exhibiting low thermal expansion, low heat sag and high DOI on painted parts. ApplicationTPP 608 is designed specifically for automotive fascia.. |
|||
| CTE, linear | 45.0 - 50.0 µm/m-°C | 25.0 - 27.8 µin/in-°F | |
| Master Bond EP30M4 Chemically Resistant Two Component Epoxy System Master Bond Polymer System EP30M4 is a two component epoxy system for high performance bonding, sealing and encapsulation. This system features a forgiving 100 to 60 mix ratio by weight. EP30M4 resi.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 23.0 - 260 °C |
25.0 µin/in-°F @Temperature 73.4 - 500 °F |
ASTM D696 |
| Daelim H&L Plavis-G15 DF 15% Graphite Filled Aromatic Polyimide Bearing Direct Formed. Plavis-G-15: Graphite 15 wt% filled, Self lubricating grade for wear and friction applications.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 ca.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 23.0 - 260 °C |
25.0 µin/in-°F @Temperature 73.4 - 500 °F |
ASTM D696 |
| Daelim H&L Plavis-G15 ISO 15% Graphite Filled Aromatic Polyimide Bearing Isostatically Molded. Plavis-G-15: Graphite 15 wt% filled, Self lubricating grade for wear and friction applications.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded .. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 50.0 - 200 °C |
25.0 µin/in-°F @Temperature 122 - 392 °F |
DIN 53 752 |
| Ensinger TECASINT 4011 Polyimide, Yellow (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel.. |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | Below Tg |
| Epoxy Technology EPO-TEK® ED1020 Epoxy Preliminary Product Information SheetMaterial Description: A single component, silver-filled epoxy designed for low power semiconductor LED die attach applications. Its unique features include exce.. |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | Below Tg |
| Epoxy Technology EPO-TEK® OD2002 High Temperature Epoxy Material Description: High Tg version of EPO-TEK®353ND with low modulus and good toughness. Replacement for EPO-TEK® 364. Complies with USP Class VI biocompatibility standards.Information Provid.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
|
| Cotronics 4420 One-Part Epoxy |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Asahi Kasei Thermylene® P1-20FG-2703 20% Glass Fiber Reinforced, Impact Modified Information provided by Asahi Thermofil |
|||
| CTE, linear | 45.0 - 220 µm/m-°C | 25.0 - 122 µin/in-°F | Average value: 143 µm/m-°C Grade Count:24 |
| Overview of materials for Polyether Ester Elastomer This property data is a summary of similar materials in the MatWeb database for the category "Polyether Ester Elastomer". Each property range of values reported is minimum and maximum values of appr.. |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | ASTM E831 |
| Addiplast Addinyl C2 V20 Nylon 66/6, 20% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast. |
|||
| CTE, linear | 45.0 - 108 µm/m-°C | 25.0 - 60.0 µin/in-°F | Average value: 87.4 µm/m-°C Grade Count:7 |
| Overview of materials for Acetal Copolymer, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Glass Bead Filled". Each property range of values reported is minimum and maximum valu.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
25.0 µin/in-°F @Temperature -22.0 - 176 °F |
Borealis Method |
| Borealis Daplen™ EF209AE Polypropylene TPO Compound Daplen™ EF209AE is a 20% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties, gives a good surface q.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
|
| Cosmic Plastics 6160 Mineral Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
|
| Cosmic Plastics D44 Mineral Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||