Cosmic Plastics 6160 Mineral Filled Ortho Diallyl Phthalate Molding Compound
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP), Cast, Mineral Filler , Filled/Reinforced Thermoset |
| Manufacturer | Cosmic Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cosmic Plastics 6160 Mineral Filled Ortho Diallyl Phthalate Molding Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.84 g/cc | 0.0665 lb/in³ | |
| Water Absorption | 0.40 % | 0.40 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | |
| Flexural Strength | 76.0 MPa | 11000 psi | |
| Compressive Strength | 155 MPa | 22500 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | Heat Distortion temperature |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | |
| Dielectric Constant | 4.3 @Frequency 1e+6 Hz |
4.3 @Frequency 1e+6 Hz |
Wet |
| 4.5 @Frequency 1000 Hz |
4.5 @Frequency 1000 Hz |
Wet | |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.013 @Frequency 1000 Hz |
0.013 @Frequency 1000 Hz |
Wet |
| 0.017 @Frequency 1e+6 Hz |
0.017 @Frequency 1e+6 Hz |
Wet | |
| Arc Resistance | 135 sec | 135 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 165 °C | 275 - 329 °F | Molding temperature |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2003 TI Polypropylene
- ExxonMobil Santoprene® 111-55 Thermoplastic Elastomer (discontinued **)
- Kazanorgsintez Cosintol-247
- Garlock GYLON® 3510 PTFE Gasketing, Barium Sulfate Filler
- Kolon SPESIN® KP515FLBL High Impact PBT Alloy Resin
- Techmer ES Electrablend® PA6/6 C10 BK 10% Carbon Filled
- SABIC Innovative Plastics LNP THERMOCOMP JX97000 PES (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP NF002 PC+ABS (Asia Pacific)
- BASF Neopolen® P 9435 0.06 g/cc Core density; Expanded Polypropylene (Europe)
- Axiall 38951 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved