- Asahi Kasei Thermylene® P1-20FG-2703 20% Glass Fiber Reinforced, Impact Modified
Asahi Kasei Thermylene® P1-20FG-2703 20% Glass Fiber Reinforced, Impact Modified
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P1-20FG-2703 20% Glass Fiber Reinforced, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength, Yield | 68.9 MPa | 10000 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 97.9 MPa | 14200 psi | ASTM D790 |
| Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE Z500 Thermoplastic Elastomer, SEBS-based
- Palm Labs Adhesives TURBO-LOCK SERIES 10 Anaerobic Thread Locking Compound
- Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F)
- Solvay TECHNYL® A 216 V20 PA66, 20% glass fiber, DRY
- A. Schulman POLYBATCH™ White HS8350 Concentrate Based In Impact Polystyrene
- Dow Corning SILASTIC® LS 5-2060 FLUOROSILICONE RUBBER
- Asahi Kasei Thermylene® P6-30FG-0708 30% Glass Fiber Reinforced, High Impact
- 3M Scotchkote™ 162HB Epoxy Coating
- Bulk Molding Compounds BMC SLC 2000 Glass Reinforced Polyester
- Saint-Gobain Chemfab® 5 Premium PTFE-Coated Glass
Copyright © lookpolymers.com All Rights Reserved