Cosmic Plastics D44 Mineral Filled Ortho Diallyl Phthalate Molding Compound
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP), Cast, Mineral Filler , Filled/Reinforced Thermoset |
| Manufacturer | Cosmic Plastics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cosmic Plastics D44 Mineral Filled Ortho Diallyl Phthalate Molding Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | |
| Water Absorption | 0.40 % | 0.40 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | |
| Flexural Strength | 76.0 MPa | 11000 psi | |
| Compressive Strength | 165 MPa | 23900 psi | |
| Izod Impact, Notched | 0.230 J/cm | 0.431 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | Heat Distortion temperature |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | |
| Dielectric Constant | 4.4 @Frequency 1e+6 Hz |
4.4 @Frequency 1e+6 Hz |
Wet |
| 4.7 @Frequency 1000 Hz |
4.7 @Frequency 1000 Hz |
Wet | |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.010 @Frequency 1000 Hz |
0.010 @Frequency 1000 Hz |
Wet |
| 0.017 @Frequency 1e+6 Hz |
0.017 @Frequency 1e+6 Hz |
Wet | |
| Arc Resistance | 135 sec | 135 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 165 °C | 275 - 329 °F | Molding temperature |
Users viewing this material also viewed the following:
- PolyMirae Moplen EP300R Injection Molding Grade Polypropylene
- Mitsubishi Iupilon® S3001R 16.5 MFI FDA Compliant Polycarbonate With Release
- Multibase Multi-Flex® TPE A 5010 BLK
- Multibase Multi-Flamâ„¢ 0302 PP NH Polypropylene
- Saint-Gobain CHR® M69 Polyester Film Backing Acrylic Adhesive Pressure Sensitive Tape
- DSM Akulon® M-1016 (Cond.) 33% Glass Reinforced Nylon 66 (North America)
- DuPont Teijin Films Teijin® Tetoron® U4 Polyester Film, 63 Gauge
- 3M 4504 Foam Tape
- Arlon LW50125R##-P1 0.050" (1.27 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
- Chosun Refractories B-5 Insulating Firebrick
Copyright © lookpolymers.com All Rights Reserved