Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75 |
Nilit FRIANYL A63 TF-GV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass fiber reinforced Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C @Thickness 3.20 mm |
455 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics EXTEM XH1005F TPI Resin (Europe-Africa-Middle East) High Heat Amorphous TPI Blend, Tg 267C, High Continuous Use Temperature (CUT). EFSA Food Contact Approved. Material is UL listed. This material is RoHS compliant and also halogen free according VDE/.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Unannealed; ASTM D648 |
Ravago Manufacturing Americas Hylon® N1040MGHL Nylon 6/6 (DAM) Information provided by Ravago. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Unannealed; ASTM D648 |
Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stabi.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
Lanxess Durethan® DP AKV 30 X HR EF 900116 Nylon 66, 30% Glass Fiber PA 66, injection molding grade, 30% glass fibers, hydrolysis and good heat-ageing resistance, good flowability (Easy Flow) |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
Kolon KOPA® KN3321G10V0L G/F Reinforced & Flame Retardant Nylon 66 High flame resistant, high toughness, dimensionally stableApplications A variety of connectorsInformation provided by API-Kolon. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | |
LATI Latamid 66 H2 G/25-V0HF1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Very good mechanical properties. Very good electrica.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Unannealed; ASTM D648 |
Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA), 25% Glass Fiber (Dry) Amodel® AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional s.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP THERMOCOMP RF002 PA 66 LNP THERMOCOMP* RF002 is a compound based on Nylon 66 resin containing 10% Glass Fiber. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-93 |
Wellman Wellamid® GFT13-66 XE-WT1 13% Glass Filled, Toughened Nylon 66 Description: Glass Filled, Toughened Nylon 66Information provided by Wellman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® GV-5H EF black 9915 PA*-GF50 Product description: Grivory GV-5H black 9915 is a 50% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline Polyamide with partially aromatic copolyami.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® GV-5H PA*-GF50 Product description: Grivory GV-5H natural is a 50% glass-fiber reinforced engineering thermoplastic material based on a combination of semi-crystalline Polyamide with partially aromatic copolyamide.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® GVN-35H black 9915 PA*-GF35 Product description: Grivory GVN-35H is a 35% glass-fiber reinforced, impact-modified engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic c.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® TSG-30/4 PA666-GF30 Product description: Grilon TSG-30/4 is a heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 30% glass fibers. Grilon TSG-30/4 has the following important properties: Good flo.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | DAM; ISO 75-1/-2 |
DuPont Performance Polymers Minlon® FE6190 BK086 Nylon 66 Minlon® FE6190 BK086 is a 36% mineral/glass reinforced, heat stabilized, black polyamide resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75 |
Eurotec® Tecopet® PT70 GR45 NL100 PR PET, 45% glass fiber reinforced, heat stabilized, natural, fast crystallization grade Information provided by Eurotec® |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® GV-6H PA*-GF60 Product description: Grivory GV-6H natural is a 60% glass-fiber reinforced engineering thermoplastic material based on a combination of semicrystalline Polyamide with partially aromatic copolyamide... |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Annealed 0.125 inch thick specimen; ASTM D648 |
Solvay Specialty Polymers Supradel® HTS-2400 High Temperature Sulfone Resin
(discontinued **) SUPRADEL HTS-2400 is a high-temperature, high-performance, amorphous, sulfone polymer. With a glass transition temperature of 245°C and heat deflection temperature of 235°C, this resin extends the.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-2/AF |
Addiplast Addinyl C2 ZV40 Nylon 66/6, 40% Glass Filled Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-93 |
Wellman Wellamid® FRGF1850-N1 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant All information provided by Wellman Engineered Resins. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | >= 235 °C | >= 455 °F | ASTM D648-61 |
Budd Hi-Flex® SMC
(discontinued **) Parts requiring high strength and dimensional stability, excellent surface smoothness without sink marks; parts to be painted requiring an automotive-type finish.Data provided by the manufacturer. |