Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA), 25% Glass Fiber (Dry)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA), 25% Glass Fiber (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stability, chemical resistance and ductility. This resin has a high heat deflection temperature and a high flexural modulus, with greater tensile elongation than untoughened glass-reinforced PPA.Features: Good Chemical Resistance; Good Dimensional Stability; Heat Stabilized; High Heat Resistance; Impact ModifiedUses: Appliance Components; Appliances; Automotive Applications; Automotive Electronics; Automotive Under the Hood; Bearings; Connectors; Fuel Lines; General Purpose; Housings; Industrial Applications; Industrial Parts; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal ReplacementInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Automotive Specifications ASTM D4000 PA123 G25; ASTM D4000 PPA0111 G25 KD160 KN075 LD002 PN080 YI250; ASTM D6779 PA123G25; ISO 1874 PA6T/6I/66-HI, MH, 12-080, GF25Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ISO 1183
Filler Content 25 %
25 %
Glass Fiber
Water Absorption 0.20 %

@Time 86400 sec
0.20 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 174 MPa
25200 psi
ASTM D638
190 MPa
27600 psi
ISO 527-2
Elongation at Break 2.5 %
2.5 %
ISO 527-2
3.2 %
3.2 %
ASTM D638
Tensile Modulus 8.48 GPa
1230 ksi
ASTM D638
8.89 GPa
1290 ksi
ISO 527-2
Flexural Strength 240 MPa
34800 psi
ISO 178
Flexural Yield Strength 255 MPa
37000 psi
ASTM D790
Flexural Modulus 7.58 GPa
1100 ksi
ASTM D790
7.79 GPa
1130 ksi
ISO 178
Izod Impact, Notched 1.20 J/cm
2.25 ft-lb/in
ASTM D256
Izod Impact, Unnotched 11.0 J/cm
20.6 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 8.80 kJ/m²
4.19 ft-lb/in²
Type 1, Notch A; ISO 180
Charpy Impact, Notched 0.880 J/cm²
4.19 ft-lb/in²
Type 1, Edgewise; ISO 179
Dart Drop, Total Energy 13.8 J
10.2 ft-lb
Instrumented; ASTM D3763
Thermal Properties Metric English Comments
Melting Point 311 °C
592 °F
ASTM D3418
311 °C
592 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 279 °C
534 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 235 °C
455 °F
Unannealed; ASTM D648
280 °C
536 °F
Unannealed; ISO 75-2/A
Processing Properties Metric English Comments
Processing Temperature 79.4 °C
175 °F
Hopper
Rear Barrel Temperature 304 - 318 °C
579 - 604 °F
Front Barrel Temperature 316 - 329 °C
601 - 624 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 135 °C
275 °F
Drying Temperature 121 °C

@Time 14400 sec
250 °F

@Time 4.00 hour
Moisture Content <= 0.10 %
<= 0.10 %
Descriptive Properties Value Comments
Additive Heat Stabilizer
Impact Modifier
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant