Lanxess Durethan® DP AKV 30 X HR EF 900116 Nylon 66, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP AKV 30 X HR EF 900116 Nylon 66, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, injection molding grade, 30% glass fibers, hydrolysis and good heat-ageing resistance, good flowability (Easy Flow)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.324 g/cc | 0.04783 lb/in³ | ISO 1183 |
| Water Absorption | 5.9 % | 5.9 % | Test Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0043 cm/cm | 0.0043 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0082 cm/cm | 0.0082 in/in | ISO 294-4, 2577 |
| Melt Flow | 42 g/10 min @Load 5.00 kg, Temperature 290 °C |
42 g/10 min @Load 11.0 lb, Temperature 554 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | Conditioned; ISO 527-1/-2 |
| 135 MPa | 19600 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1/-2 |
| 8.5 % | 8.5 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 4.50 GPa | 653 ksi | Conditioned; ISO 527-1/-2 |
| 8.00 GPa | 1160 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 263 °C | 505 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 250 °C | >= 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87350 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Pacific Sintered Materials SS-410-R 410 Stainless Steel Powdered Metal
- Nilit Nilamid A3 H5 G6 30% Glass Reinforced PA66
- Abatron AboCast 8-16/Abocure 8-16 Epoxy (discontinued **)
- SGL Carbon Group EK 2230 Carbon Graphite
- Samyang Trimma® FT6120 I[R] PMMA, Transparent
- Westlake LF1020 Butene Linear Low Density Polyethylene
- CP-Polymer-Technik Wellamid® 6600 GV 5 HWCP 5% Glass Fiber Nylon 66, Heat Stabilized, Dry
- Aaron Industries AAROPRENE® AEPC 5000-4 Engineered Polycarbonate Resin
- Overview of materials for Acrylic, Optical Grade, Molded
Copyright © lookpolymers.com All Rights Reserved