- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 189 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 189 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | 120°C/h; ASTM D 648 |
| Polimeri Europa Edistir RT 461F Polystyrene High impact, heat resistant polystyrene with good stiffness. Recommended for improving the thermal performance of injection moulded technical parts which are submitted to high temperature in service.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycolac® INP572 ABS+SAN High molecular weight SAN, functions as a carrier resin for color concentrates. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to pro.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycolac® INP576 ABS Can be used as compounding additives for polymer blends. Medium molecular weight SAN. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® INP576 ABS+SAN Can be used as compounding additives for polymer blends. Medium molecular weight SAN. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® C7410 PC+ABS (Asia Pacific) Cycoloy* C7410 resin is a talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® CM6220 PC (Asia Pacific) CYCOLOY CM6220 resin is a mineral filled grade featuring of high modulus (6GPa), good flow and ductility, low warpage. It is of non-Br & non-Cl flame retardant systems intended to meet thin wall fla.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Lexan® DMX9254 PC (Asia Pacific) Lexan* DMX9254 resin is an injection moldable PC copolymer/ABS blend. This resin combines excellent scratch resistance with high flow and ductility. It contains non-brominated and non-chlorinated fl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Lexan® DMX9254 PC (Europe-Africa-Middle East) Lexan* DMX9254 resin is an injection moldable PC copolymer/ABS blend. This resin combines excellent scratch resistance with high flow and ductility. It contains non-brominated and non-chlorinated fl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP FARADEX AS002 ABS (Asia Pacific) LNP* Faradex* AS002 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Cycolac® DL100 ABS (Europe-Africa-Middle East) CYCOLAC DL100 is a high heat, high impact, low emissions ABS/PC blend. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | ASTM D648 |
| Ineos Nova Zylar® 220 Clear Impact Modified Acrylic Copolymer
(discontinued **) Features:High clarity Good elongation Styrenic processing advantages Excellent property retention after gamma and ETO sterilization Meets USP XXIII specifications for Class VI plasticsApplications:D.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | |
| Inchem Phenoxy PKFE Phenoxy PKFE - polyhydroxy ether of Bisphenol A. Originally developed by Union Carbide. Produced by InChem Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LI911 ASA Description: Good Weatherability, High FlowApplication: Air-conditioner grill, Sawing Machine Cover, Electric/Electronic ApplicationsCAS: 26299-47-8Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP KL004A ACETAL HOMOPOLYMER (Europe-Africa-Middle East) LNP* LUBRICOMP* KL004A is a compound based on Acetal Homopolymer resin containing PTFE. Added features include: Internally Lubricated |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KP004XXP Acetal Copolymer LNP LUBRICOMP* KP004XXP is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS LNP THERMOCOMP* AH0230A is a compound based on ABS resin. Added feature of this material is: High Specific Gravity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® WR-9120 J ASA, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | ASTM D648 |
| Samyang Tramid® 210F Polyamide, High Productivity Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.210F is a high productivity grade.Applications:ConnectorsCable tiesHarness clipsT.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Xenoy® X5300WX PBT+PC (Asia Pacific) Unreinforced, opaque PBT+PC alloy. Chemical resistance and good mechanical performance. UV-stabilized. Excellent weatherability. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | ASTM D648 |
| Denka TX-400S Transparent Resin Polymer (MS resin) Methyl Methacrylate Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F | Unannealed; ASTM D648 |
| Entec Hyrene® PSCRY 14 General Purpose Polystyrene Available in North America Features: General PurposeRoHS Compliant Form: Pellets Information provided by Entec |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F | 0.125 in bar Unannealed/Conditioned 40 hours at 23°C; ASTM D648 |
| Diamond Polymers ASA TW-17 Description: ASA Weatherable Polymer, Injection Molding Grade, High HeatInformation provided by Diamond Polymers, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F | |
| Aclo Accutech ABS ABS833G10L Glass Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0334G5M25CL Glass/Mineral Reinforced Coupled |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F | |
| Aclo Acculoy PCA083L Polycarbonate ABS Alloy |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F | Annealed; ASTM D648 |
| American Polymers API 425 Polystyrene API 425 is a medium impact grade of polystyrene for injection molding. API 425 has good gloss, easy flow and fast cycling properties.Applications: API 425 is widely used in cosmetic packaging, food.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | ASTM D648 |
| LG Chemical HI835H PMMA, Impact Resistant Grade Molding granule designed for greater impact strength combined with the outstanding properties of conventional acrylic materialsFeatures: Excellent transparency and eleganceWeather resistance and che.. |
|||