Aclo Acculoy PCA083L Polycarbonate ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade , Polycarbonate (PC) |
| Manufacturer | Aclo Compounders |
| Trade Name | Acculoy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Acculoy PCA083L Polycarbonate ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.111 g/cc | 0.04014 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | MD; ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| 17 g/10 min @Load 5.00 kg, Temperature 250 °C |
17 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D648 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 33 % | 33 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.700 GPa | 246.5 ksi | ASTM D638 |
| Flexural Strength | 81.01 MPa | 11750 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 5.82 J/cm | 10.9 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD: 8-15 nm COOH Functionalized Aligned Multi-Walled Carbon Nanotubes
- Permabond 932 Cyanoacrylate
- Taiwan PU Corporation PTMG CPU-100L Polyurethane Casting Elastomer
- A. Schulman LP544-01 High-Density Copolymer Polyethylene
- Wico Plast Wicolon 407 Polycarbonate, U.V. Stabilized
- Fainplast Compounds GSK 0637/AL Flexible PVC, Injection Molding, Lead Free
- Dow TUFLIN™ HS-7094 NT 7 Linear Low Density Polyethylene Resin
- BASF Lupragen® N 107 Dimethylaminoethoxyethanol
Copyright © lookpolymers.com All Rights Reserved