Aclo Accutech Polypropylene Homopolymer HP0334G5M25CL Glass/Mineral Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass/Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0334G5M25CL Glass/Mineral Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | MD; ASTM D955 |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 72 | 72 | ASTM D785 |
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 3.499 GPa | 507.5 ksi | ASTM D638 |
| Flexural Strength | 53.0 MPa | 7690 psi | ASTM D790 |
| Flexural Modulus | 3.499 GPa | 507.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.502 J/cm | 0.940 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 277 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® PC2200 PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP LUBRICOMP DFL34XXP PC (Europe-Africa-Middle East)
- MetaFoam Copper Foam
- Mitsubishi Xantar® G4F 23 R Polycarbonate-20% Glass Reinforced
- Tisan TISLAMID® 6 30% Glass Filled Impact Modified, Heat Stabilized Nylon 6
- Covestro Bayflex® 110-50 Polyurethane Elastomeric RIM, 15% Mineral Filled, MDI-based 2-Component Liquid System
- Bapolene® 4071 Polypropylene, Fiber/Injection Grade
- Aremco Corr-Paint™ CP4020 High Temperature Protective Coating Silicone, Aluminum Filled
- ConocoPhillips 2 Bentone Grease NLGI No. 2
Copyright © lookpolymers.com All Rights Reserved