- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 131 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 131 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Plastcom SLOVASTER® B FRN 3 LS PBT, flame retarder, light stable FeaturesPBT basic type for injection molding. Melt is characterised by outstanding fluidity, which enables injection molding of complicated and divided products also on multiple molds. Anisotropy of.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 |
| Dow INSPIRE™ D7030EZ Thermoplastic Polyolefin
(discontinued **) Information provided by DowThe Inspire brand was spun off from Dow Chemical to Styron in 2010, although this grade had previously been removed from Dow's standard product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1, -2 |
| Lanxess Pocan® B 1701 000000 PBT PBT, non-reinforced, extrusion, food contactInformation provided by LANXESS. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75/Af |
| Solvay TECHNYL® C 507XT PA6, DRY Description: Unreinforced polyamide 6, heat stabilized, very high viscosity, for extrusion.Available in: Europe Product Applications: It is suitable for extruded semi-finished products, such as: Rod.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/12 05007 Nylon 612 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer and LubricantFeatures: Lubricated and Heat StabilizedInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Valox® FXV310SK PBT VALOX FXV310SK is an unreinforced PBT injection moulding Visualfx* resin with high flow characteristics and containing a metal sparkle. Applications: automotive bezels and appliances. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C @Thickness 3.20 mm |
131 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY W3000XXJ PBT LNP* STAT-LOY* W3000XXJ is a compound based on PBT. Added features of this grade include: Anti-Stat, Colorable, Healthcare |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene DescriptionPolyfort® FPP 1237 is a 20% CAC03 filled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| A. Schulman PP 3486-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3486-01 is a special homopolymer polypropylene designed with long term heat aging formula for appliance application.ApplicationThis product is for injection molded applic.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-93 |
| Wellman Wellamid® 42LN2-NBK2 Nylon 6, General Purpose All information provided by Wellman Engineered Resins. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | 120°C per hour; ISO 75-2 |
| Total PPH 3051 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 3051 is homopolymer.ApplicationATOFINA Polypropylene PPH 3051 is intended for the extrusion of flat bioriented films for food packaging or high strength adhesive tapes. Inf.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | 120°C per hour; ISO 75-2 |
| Total PPH 7069 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 7069 is homopolymer.ApplicationATOFINA Polypropylene PPH 7069 is characterized by medium fluidity for extrusion of continuous filament (CF) and bulk continuous filament (BC.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-2 |
| Borealis Daplen™ EG102AI Polypropylene Compound 15% Mineral Filled Daplen EF102AI is a 15% mineral filled polypropylene compound intended injection molding. EG102AI is an easy flow grade, specially developed for the car industry. Daplen EF102AI has been developed.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-93 |
| Wellman Wellamid® 42L-XE-N Nylon 6, Engineering Grade All information provided by Wellman Engineered Resins. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | 120°C/hr; ASTM D 648 |
| Cossa Polimeri ESTAPROP 1006 V2 H Flame Retardant Polypropylene PP copolymerFlame retardant class V2, PBDE and antimony trioxide free, no blooming, low smoke emission, good physical and mechanical characteristicsInformation provided by Cossa Polimeri S.r.l. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 |
| DSM Arnite® T08 200 (extrusion) PBT (European and Asian Grade) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® TSZ 1 PA666 Product description: Grilon TSZ 1 is a heat stabilized, normal viscosity, impact modified PA66 + PA6 injection molding grade. Grilon TSZ 1 has the following important properties: Excellent flow beha.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 7301 NC010 Nylon 6
(Unverified Data**) Zytel® 7301 NC010 is a general purpose, unlubricated polyamide 6 resin for extrusion applications.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Clariant Renol PA233HT Nylon 6, Improved Processability, Easily Colorable, Highly Toughened Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 |
| Eurotec® Tecolen® CP20 MF20 NL XC30 PPCP, 20% mineral filled, flame retardant - halogen (RoHS compliant), heat stabilized, natural Information provided by Eurotec® |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| BASF Novolen® 1184 L Polypropylene Nucleated grade with high processing stability containing antistatic for thermoformed parts.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| BASF Ultramid® 8351 HS BK 102 PA6 (Dry) Description: Ultramid 8351 HS BK-102 is a heat stabilized, pigmented black, impact modified type 6 nylon graft copolymer developed for injection molding applications requiring a high level of toughn.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 |
| A.D. Compound Adene NTFAG Copolymer 20% Talc Filled Polypropylene Information provided by A.D. Compound |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | 90 Minute UV Cure; ASTM D648 |
| 3D Systems Accura® SI 40 Plastic for the SLA® 250 System Accura 40 "Ar" or "Hc" type materials - for the SLA 250 system. Mimics Nylon 6:6ApplicationsHigh temperature testing:Under hood bolt-on testingWind tunnel testingHVAC testingPrototyping and testing .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| BASF Novolen® 1101 N Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 - 130 °C | 131 - 266 °F | Average value: 81.1 °C Grade Count:24 |
| Overview of materials for Polypropylene with 30% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Mica Filler". Specific grades with primary filler content between 25% and 34% are.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 |
| Polyram RamSter PF801 PBT, High Impact Modified High impact modified PBT for injection molding applications.Information provided by Polyram. |
|||