Techmer ES Luriblend® PA6/12 05007 Nylon 612
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Unreinforced |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6/12 05007 Nylon 612.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer and LubricantFeatures: Lubricated and Heat StabilizedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Water Absorption | 0.25 % @Time 86400 sec |
0.25 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 3.17 mm |
0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength, Yield | 60.7 MPa | 8800 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm |
0.800 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C | 44.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-2 | V-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- NextGen Adhesives G907-24 Structural Epoxy Adhesive
- Shakespeare HPA-14 diameter 0.7 mm PPS Monofilament
- Valley Adhesives EM-600 High Temperature Application Glue Stick
- Polyram PlusTek PA865G6 Nylon 6.6, 30% Glass Fiber
- A. Schulman POLYBATCH™ White P8555 SD Concentrate Based In Homopolymer Polypropylene
- Chengdu Polyster 8502 High Performance Grade TPV
- Dow Corning S50 LIQUID SILICONE RUBBER KIT
- BASF Novolen® 1102 H Polypropylene
- Universal Wire Works 1100 (AMS 4180) Aluminum Alloy Filler Metal
- Saint-Gobain Rulon® J Grade Bearing/Seal PTFE
Copyright © lookpolymers.com All Rights Reserved