Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | ASTM D648 |
Ravago Manufacturing Americas Hybrid S555 ABS + Polycarbonate Alloy Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Rava.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | Unannealed; ASTM D648 |
M. Holland Company GS230 Polystyrene, General Purpose High heat resistanceGood processabilityHigh strengthApplications: BottlesBusiness equipmentMedical applicationsPackaging |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | Unannealed; ASTM D648 |
Techmer ES Plastiblend® ABS 8006 Availability: North AmericaForms: PelletsProcessing Method: Sheet ExtrusionInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C @Thickness 6.35 mm |
201 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
Samsung Cheil Industries Starex® WR-9330I Heat Resistant Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C @Thickness 6.35 mm |
201 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
Samsung Cheil Industries Starex® WR-9330I Heat Resistant Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C @Thickness 3.17 mm |
201 °F @Thickness 0.125 in |
annealed; ASTM D648 |
Sumitomo Chemical Sumipex® BF3 Acrylic Resin, GP Blow Molding Grade Product CharacteristicsExcellent WeatherabilityHigh TransparencyGood Heat ResistanceInformation provided by Calsak Corporation |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | ASTM D648 |
Ensinger TECACRYL® TECACRYL® offers excellent weather resistance, high light transmission, high mechanical strength, high surface hardness and mar resistance, good melt flow rate, and versatile colorability due to cr.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 2510 Description: Injection Molding Grade, Medium Impact, Super High FlowInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 2512 Description: Injection Molding Grade, Medium Impact, High FlowInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
Diamond Polymers ABS 3501 GF-10 Description: Reinforced Grade, 10%Glass FilledInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 3501 Natural 1050 Description: Natural, Injection Molding Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 3501E Description: Extrusion Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 3501E Natural 1050 Description: Extrusion Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 3502E Description: Extrusion Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 4500R Description: Injection Molding Grade, Medium ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 7600B Description: Blow Molding Grade, Extra High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ASA S170 Description: ASA Weatherable Polymer, Injection Molding Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ASA S710 Description: ASA Weatherable Polymer, Injection Molding Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | |
Aclo Accutech ABS ABS832G30L Glass Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | |
Aclo Accutech ABS ABS833G20L Glass Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | |
Aclo Accutech ABS ABS834G40L Glass Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 2510 Description: Injection Molding Grade, Medium Impact, High FlowInformation provided by Diamond Polymers, Inc. |