Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C @Thickness 3.18 mm |
150 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ Vinyl Rigid Extrusion 87736 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
RheTech Products FRP300-00 20% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Natural Applications: Electrical component housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
RheTech Products FRP300-01 20% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Black Applications: Electrical component housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
RheTech Products HP519-00 26% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural Applications: Interior trim moldingsSill platesAir ductsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
RheTech Products M12P100-01 12% Mica Reinforced Polypropylene, Black Applications: Fan shroudsAir ductsFiller panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
RheTech Products T30P200-01BG 30% Talc Reinforced Polypropylene Copolymer, Black, Blow Molding Grade Applications: HVAC ductsSeat backsFlipper panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
Polymer Resources NY6-GP1-[color]H Nylon, General Purpose, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
Ravago Manufacturing Americas Hylon® N2000STHL Nylon 6 (DAM) Information provided by Ravago. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
Fiberfil® PP-61/TC/20 Polypropylene Copolymer, 20% Talc Information provided by FIBERFIL Engineered Plastics |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed (0.250"); ASTM D648 |
LTL Color Compounds ColorFast® NYA1000 Nylon/ABS Alloy Nylon/ABS alloy with high ductility and excellent chemical resistanceAll information provided by LTL Color Compounders, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
Techmer ES Elastoblend® PA6/66 IM 6040 MB Availability: North AmericaForms: PelletsAdditive: Nucleating Agent, Heat Stabilizer, Lubricant and Impact ModifierFeatures: Copolymer, Nucleated, Heat Stabilized, Lubricant and Impact ModifiedInfor.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® HDPE TM30 30% Talc Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 30% Filler by WeightInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
Spartech PP5130 Talc Filled Homopolymer Offers an excellent balance of processing improvement and high levels of stiffness and heat deflection temperatureInformation provided by Spartech |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
Spartech Royalite DKE 400 PVC/Acrylic Fire Rated Sheet Description: Fire Rated SheetInformation provided by Spartech. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
Techmer ES Plastiblend® PA6/6,6 IM 5050 BK MB Nylon 6/66 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Copolymer, Impact Modified and LubricatedAppearance: BlackProcessing Metho.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
Techmer ES Plastiblend® PA6/6,6 IM 6040 BK MB Nylon 6/66 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Copolymer, Impact Modified and LubricatedAppearance: BlackProcessing Metho.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM Test |
Styrolution Terblend® N NM-19 ABS/PA6 (Dry) Terblend N NM-19 is a UV stabilized ABS/PA6 blend combining very high impact strength, even at low temperatures with an excellent processability and surface appearance.Information provided by STYROL.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
Ecomass® 3608TU96 Tungsten Filled Polyethylene Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applicationsHigh Specific GravityTungsten Powder Filled Polyethylene (HDPE)Information provided by Technical Polymers |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
Ecomass® 3620BX60 18% Borated Polyethylene (HDPE) 18% Borated Polyethylene (HDPE), Product Form - Pellets, No Pre-Drying RequiredProcessing Method: Injection Molding, Compression MoldingNeutron Shielding ApplicationsInformation provided by Technic.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D-648 |
Axiall 3027 Rigid PVC, Extrusion Georgia Gulf 3027 is a powder blend designed as a substrate base for coextruded profiles.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |