Spartech PP5130 Talc Filled Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Spartech |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Spartech PP5130 Talc Filled Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Offers an excellent balance of processing improvement and high levels of stiffness and heat deflection temperatureInformation provided by Spartech
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc @Temperature 22.8 °C |
1.15 g/cc @Temperature 73.0 °F |
ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | 0.125inch wall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.7 MPa | 4600 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Modulus | 2.14 GPa | 310 ksi | secant; ASTM D790 |
| 2.76 GPa | 400 ksi | tangent; ASTM D790 | |
| Izod Impact, Notched | 0.294 J/cm @Temperature 22.8 °C |
0.550 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | >= 1.36 J @Temperature 22.8 °C |
>= 1.00 ft-lb @Temperature 73.0 °F |
ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 260 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 42 % | 42 % | 60°; ASTM D523 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 21-8015 Polyamide 6/6T, with carbon fiber
- KKPC KOSYN 1500 Styrene Butadiene Rubber
- Momentive Performance Materials RTV102 White Adhesive Sealant, High Strength Paste
- Lucent Polymers CPP-220 Polypropylene, 20% Calcium Carbonate Filled, Impact Modified
- Kuraray SEPTON® A4 Hot Melt Adhesive
- Solvay Specialty Polymers Ajediumâ„¢ KT-820 Polyetheretherketone (PEEK)
- SABIC Innovative Plastics Xenoy® X3515 PC+POLYESTER (Asia Pacific)
- DuPont Performance Polymers Zytel® FR70M30V0 BK010 Nylon 66 (Unverified Data**)
- Aclo Accucomp Polypropylene CPO425BAV Automotive Approved Copolymer Expandable Grade
- Akro-Plastic Akromid® A3 GF 60 (2424) PA 6.6 Conditioned, 60% Glass Filled
Copyright © lookpolymers.com All Rights Reserved