- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 55.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 55.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75/2Af |
| Radici Radilon® SHS (dry) Nylon 6 General PurposeInformation provided by Radici group. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Plastcom SLOVASTER® B FRN 3 PBT, flame retarder FeaturesPBT basic type for injection molding. Melt is characterised by outstanding fluidity, which enables injection molding of complicated and divided products also on multiple molds. Anisotropy of.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 |
| Lanxess Pocan® KU 2-7205 000000 PBT PBT, non-reinforced, injection molding, extrusion, flame retardant |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C @Thickness 3.20 mm |
131 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT LNP LUBRICOMP* WL004 is a compound based on PBT resin containing 20% PTFE. Added features of this material include: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C @Thickness 3.20 mm |
131 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP WP004 PBT LNP* LUBRICOMP* WP004 is a compound based on PBT resin containing 20% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| A. Schulman PP 3488-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3488-01 is a specially formulated homopolymer polypropylene designed for large appliance injection molding. This material has excellent chemical resistance in addition t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1434 Couple Mica In Copolymer Polypropylene (25% Mineral Filled) DescriptionPolyfort® FPP 1434 is a 25% coupled mica copolymer polypropyleneInformation provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-93 |
| Wellman Wellamid® 42L-N Nylon 6, General Purpose All information provided by Wellman Engineered Resins. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | 120°C per hour; ISO 752 |
| Total PPH 6088 Polypropylene Homopolymer, Cast Film Polypropylene PPH 6088 is a homopolymer polypropylene with a Melt Flow index of 9 g/10 min for the cast extrusion of film with excellent optical properties and good sterilizability.Polypropylene PPH.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | 120°C per hour; ISO 75-2 |
| Total PPH 7069 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 7069 is homopolymer.ApplicationATOFINA Polypropylene PPH 7069 is characterized by medium fluidity for extrusion of continuous filament (CF) and bulk continuous filament (BC.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3720 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene DescriptionPolyfort® FPP 1237 is a 20% CAC03 filled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| A. Schulman POLYFLAM™ E-17338 22% CACO3 Filled Copolymer Polypropylene DescriptionPolyfort® E 17338 is a 22% filled copolymer polypropylene product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| A. Schulman PP 3486-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3486-01 is a special homopolymer polypropylene designed with long term heat aging formula for appliance application.ApplicationThis product is for injection molded applic.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Eastman Tenite 485E3720023 Butyrate Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | 120°C/hr; ASTM D 648 |
| Cossa Polimeri ESTAPROP 1006 V2 H Flame Retardant Polypropylene PP copolymerFlame retardant class V2, PBDE and antimony trioxide free, no blooming, low smoke emission, good physical and mechanical characteristicsInformation provided by Cossa Polimeri S.r.l. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | 120°C/hr; ASTM D 648 |
| Cossa Polimeri ESTAPROP 1006 V2 K Flame Retardant Polypropylene PP copolymerFlame retardant class V2, PBDE and antimony trioxide free, no blooming, low smoke emission, good physical and mechanical characteristicsInformation provided by Cossa Polimeri S.r.l. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Covestro Baydur® GS PUR Polyurethane Polyurethane casting system for the production of solid components. Pressureless casting into open or closed molds, fast demold times, good rot resistance. Combines easily with other materials.Infor.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-2/A |
| ExxonMobil Exxtral™ LNU 011 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin with high stiffness, high gloss, low discoloration and good detergent resistance for large electrical appliances such as washing machi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 |
| Eurotec® Tecolen® CP20 MF20 NL XC30 PPCP, 20% mineral filled, flame retardant - halogen (RoHS compliant), heat stabilized, natural Information provided by Eurotec® |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Arkema Group Rilsan® AESN TL Nylon 12, Flexible Tubing Grade (Conditioned) Designation ISO 1874-PA12,EHL,22-010Rigid grade for tubes extrusion. Available colors: black and natural. Light and heat stabilized.High impact strength. Good chemical resistance. Very good ability .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| BASF Novolen® 1102 H Polypropylene Grade with high processing stability for packaging tapes, film tape, fibrillated film, monofilaments, thermoformed and blow molded parts.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 |
| BASF Ultramid® B3L PA6 (Dry) Ultramid B3L is an impact-modified, easy flowing injection molding PA6 grade for fast processing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Braskem CP 204 Injection Molding Polypropylene Description: CP 204 is a high melt flow rate heterophasic copolymer with general purpose additive package. This product exhibits excellent processing performance, with good stiffness and impact stre.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Braskem H 103 Extrusion Coating Polypropylene Homopolymer Description: H 103 is a high melt flow rate additivated homopolymer used for general purposes. The product exhibits excellent processing performance on injection moulding applications. Applications:.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 |
| Azoty Tarnow™ Tarnamid® T-27 MTR Polyamide 6 - Transparent Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Transparent up to maximum 2.5 mm.Tarnamid® has the following main properties.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| BASF Novolen® 1148 RC Polypropylene Nucleated grade with antistatic agent for injection molded parts.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® CE2055 BK580 PBT
(Unverified Data**) Crastin® CE2055 is an unreinforced, low viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers |
|||