SABIC Innovative Plastics LNP LUBRICOMP WP004 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP WP004 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* WP004 is a compound based on PBT resin containing 20% PTFE/Silicone. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0900 % | 0.0900 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 5 mm/min; ASTM D638 |
| 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | Type I, 5 mm/min; ASTM D638 |
| 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 11.2 % | 11.2 % | Type I, 5 mm/min; ASTM D638 |
| 11.9 % | 11.9 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 10.7 % | 10.7 % | Type I, 5 mm/min; ASTM D638 |
| 11.3 % | 11.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.24 GPa | 325 ksi | 1 mm/min; ISO 527 |
| 2.28 GPa | 331 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
| Flexural Modulus | 2.12 GPa | 307 ksi | 2 mm/min; ISO 178 |
| 2.19 GPa | 318 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.300 J/cm | 0.562 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.70 J/cm | 5.06 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J @Temperature 23.0 °C |
1.48 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.24 | 0.24 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.13 | 0.13 | ASTM D3702 Modified |
| K (wear) Factor | 32.2 x 10-8 mm³/N-M | 16.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature -30.0 - 30.0 °C |
61.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 182 °C @Thickness 3.20 mm |
360 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 55.0 °C @Thickness 3.20 mm |
131 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Mytex Polymers AS33L-07V Polypropylene, Rubber modified, Compounded
- Precision Polymer Engineering N50M Nitrile Rubber
- Polymer Resources PPX-FR1-[color]-EN Modified-PPO, V-0 Flame Retardant, Extrusion Grade
- Iran Petrochemical (PCC) TPC - 522 FC Expandable Polystyrene
- Inhance Fluoro-Seal INHANCE® Ti--9113 Titanium Carbide Polymer Alloy
- Potters Industries A-Series P-0060 Soda-Lime Silica Technical Quality Solid Glass Spheres
Copyright © lookpolymers.com All Rights Reserved