Arkema Group Rilsan® AESN TL Nylon 12, Flexible Tubing Grade (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Extrusion/Tubing Grade
Manufacturer	Arkema
Trade Name
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Arkema Group Rilsan® AESN TL Nylon 12, Flexible Tubing Grade (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Designation ISO 1874-PA12,EHL,22-010Rigid grade for tubes extrusion. Available colors: black and natural. Light and heat stabilized.High impact strength. Good chemical resistance. Very good ability to be processed at high speed.Example applications: For general use.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.01 g/cc	0.0365 lb/in³
Melt Flow	2.5 g/10 min <br>@Load 2.16 kg,<br> Temperature 235 °C	2.5 g/10 min <br>@Load 4.76 lb,<br> Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	41.0 MPa	5950 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	8.0 %	8.0 %	50 mm/min
Tensile Modulus	1.38 GPa	200 ksi	1 mm/min
Charpy Impact Unnotched	NB	NB
	NB	NB	Low Temp
Charpy Impact, Notched	2.50 J/cm²	11.9 ft-lb/in²
	0.770 J/cm² <br>@Temperature -30.0 °C	3.66 ft-lb/in² <br>@Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	100 µm/m-°C <br>@Temperature 20.0 °C	55.6 µin/in-°F <br>@Temperature 68.0 °F
Melting Point	174 °C	345 °F	(Dry)
Deflection Temperature at 0.46 MPa (66 psi)	135 °C	275 °F
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C	131 °F
Vicat Softening Point	142 °C	288 °F	50°C/hr; 50N
Flammability, UL94	HB <br>@Thickness 1.60 mm	HB <br>@Thickness 0.0630 in
	V-2 <br>@Thickness 3.20 mm	V-2 <br>@Thickness 0.126 in

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Strength	30.0 kV/mm	762 kV/in
Comparative Tracking Index	600 V	600 V