Lanxess Pocan® KU 2-7205 000000 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Extrusion Grade , Polybutylene Terephthalate (PBT), Flame Retardant , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® KU 2-7205 000000 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, non-reinforced, injection molding, extrusion, flame retardant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0021 cm/cm | 0.0021 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0022 cm/cm | 0.0022 in/in | ISO 294-4, 2577 |
| Melt Flow | 41 g/10 min @Load 2.16 kg, Temperature 270 °C |
41 g/10 min @Load 4.76 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ISO 527-1/-2 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
| Elongation at Break | 16 % | 16 % | ISO 527-1/-2 |
| Elongation at Yield | 3.9 % | 3.9 % | ISO 527-1/-2 |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 15.0 J/cm² @Temperature 23.0 °C |
71.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 48.0 °C | 118 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
IEC 60695-11-10 |
| V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Flame retarding agent | |
| Features | Flame retardant | |
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,GFR,11-030; ISO 1043-PBT FR(17) | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Nye Lubricants 181B (SO) Synthetic Oil
- Quadrant EPP Fluorosint® 207 PTFE + mica, compression moulded (ISO Data)
- SABIC Innovative Plastics Lexan® FXD143R PC (Europe-Africa-Middle East)
- LATI Latamid 66 E21 G/15 PA 66, 15% Glass Fiber Reinforced
- Samsung Cheil Industries Starex® HR-0370F ABS, Unreinforced Heat Resistant
- A. Schulman POLYBATCH™ White LL8970 TS Concentrate Based In LLDPE
- A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene
- E-Polymers TEKAMID® TA210HS , Heat Stabilized PA66, DAM
- Dow TUFLIN™ HS-7041 NT 7 Linear Low Density Polyethylene Resin
- 3M OFM040E Outdoor UL Recognized White Polyester Label Product
Copyright © lookpolymers.com All Rights Reserved