- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 44.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 44.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ISO 75 method A |
| Quadrant EPP Cesticolor™ HD 500 Polyethylene Data provided by Quadrant Engineering Plastic Products for polymers in their European product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ISO 75 method A |
| Quadrant EPP Cestilene™ HD 500 Polyethylene Data provided by Quadrant Engineering Plastic Products for polymers in their European product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ISO 75 method A |
| Quadrant EPP Cestilene™ HD 500 R Polyethylene Data provided by Quadrant Engineering Plastic Products for polymers in their European product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ISO 75-1/-2 |
| Quadrant EPP PE 500 PE-HMW, virgin (ISO Data) This grade exhibits a good combination of stiffness, toughness, mechanical damping ability with wear- and abrasion resistance and can easily be welded. In less demanding applications with respect to.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Compression Molded; ASTM D648 |
| NOVA Chemicals Surpass® RMs244-UG Octene sHDPE Rotational Molding Film Features: Octene copolymerExceptional low temperature propertiesOutstanding stiffnessBroad processing windowSuperior whiteness for improved part appearanceEasy mold releaseNSF listed for Standards 1.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | STN EN ISO 75-2 (A) |
| Plastcom SLOVAMID 6 HI HV TS PA6 with impact modifier PA 6 higher viscosity, heat stabilized, impact modified for extrusion and blow molding. Automotive applications as air ducts and fuel filter pipes, fuel and oil containers.Information Provided by Pl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Compression Molded; ASTM D648 |
| NOVA Chemicals Surpass® RMs244-U Octene sHDPE Rotational Molding Film Features: Octene copolymerExceptional low temperature propertiesOutstanding stiffnessBroad processing windowSuperior whiteness for improved part appearanceEasy mold releaseNSF listed for Standards 1.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | |
| LyondellBasell Lupolen® 5261 Z HDPE, Blow Molding Grade Relatively high viscosity blow molding grade for rigid, stackable and highly shock resistant containers for packaging all types of hazardous materials such as flammable, corrosive, poisonous and sur.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | |
| LyondellBasell Lupolen® 5261 Z HI HDPE Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP TX97446 PU LNP* LUBRICOMP* TX97446 is a compound based on Polyurethane containing Proprietary Fillers. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C @Thickness 3.20 mm |
111 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP TH0600A PUR LNP THERMOCOMP* TH0600A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C @Thickness 3.20 mm |
111 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP TH0600A PUR (Asia Pacific) LNP THERMOCOMP* TH0600A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Stat-kon FX97333 PE LNP* Stat-kon* FX97333 is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for th.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C @Thickness 3.20 mm |
111 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Stat-kon FX97333 PE LNP* Stat-kon* FX97333 is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for th.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Stat-kon FX97333 PE (Asia Pacific) LNP* Stat-kon* FX97333 is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for th.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C @Thickness 3.20 mm |
111 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Stat-kon FX97333 PE (Asia Pacific) LNP* Stat-kon* FX97333 is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for th.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp MK001AS PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MK001AS is a compound based on Polypropylene resin containing Mineral. Added features include: Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East r.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ISO-R 75 Method A |
| Hippe PE 500 Polyethylene Tough, flexible and stiff, depending on the crystalline structure (density). Resinous surface. Excellent dielectric properties, Good resistance against solvents, acids and alkalis. Physiologicall.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Unannealed; 54°C (129°F) annealed; ASTM Data |
| Dow Prevail® 3050 ABS + Polyurethane PREVAIL® 3050 thermoplastic resin offers designers and manufacturers a combination of flexibility and low temperature toughness not previously available in an engineering thermoplastic and is used .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ASTM-D648 |
| Braskem Prisma 2910 RACO Random Polypropylene Copolymer Prisma 2910 is a high melt flow rate random copolymer designed for injection molding applications. This product offers high impact strength at low temperatures and excellent processability. Its appl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 - 127 °C | 111 - 260 °F | Average value: 82.7 °C Grade Count:8 |
| Overview of materials for High Density Polyethylene (HDPE), Extruded This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Extruded". Each property range of values reported is minimum and maxim.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ASTM D648 |
| ALM PA 860 White Nylon 11 SLS Prototyping Polymer Unfilled White PA 11 that is formulated for easy processing across all LS platforms. Tightly controlled particle distribution creates a smooth surface finish and excellent feature detail. Parts prod.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ISO 75 |
| LyondellBasell Hifax™ ETA-3163 Thermoplastic Olefin Resin Key Features: medium melt flow, medium high modulus, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, good dimensional stability, good paintability, good pro.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 - 84.0 °C | 111 - 183 °F | Average value: 64.6 °C Grade Count:3 |
| Overview of materials for ABS/Polyurethane Alloy This property data is a summary of similar materials in the MatWeb database for the category "ABS/Polyurethane Alloy". Each property range of values reported is minimum and maximum values of appropr.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 - 150 °C | 111 - 302 °F | Average value: 69.7 °C Grade Count:192 |
| Overview of materials for Polypropylene, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |
|||