SABIC Innovative Plastics LNP LUBRICOMP TX97446 PU
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP TX97446 PU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* TX97446 is a compound based on Polyurethane containing Proprietary Fillers. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.460 % | 0.460 % | 50% RH, 24 hrs; ASTM D570 |
| 0.660 % | 0.660 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm @Time 86400 sec |
0.0070 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.020 cm/cm @Time 86400 sec |
0.0080 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | Type I, 5 mm/min; ASTM D638 |
| 23.0 MPa | 3340 psi | 5 mm/min; ISO 527 | |
| Elongation at Yield | 51 % | 51 % | 5 mm/min; ISO 527 |
| 54 % | 54 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 0.410 GPa | 59.5 ksi | 1 mm/min; ISO 527 |
| 0.560 GPa | 81.2 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 13.0 MPa | 1890 psi | ISO 178 |
| Flexural Modulus | 0.350 GPa | 50.8 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 0.380 GPa | 55.1 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 2.35 J/cm | 4.40 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.1 J/cm | 22.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 95.0 kJ/m² | 45.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 45.0 J @Temperature 23.0 °C |
33.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 37.0 J | 27.3 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 124 µm/m-°C @Temperature -30.0 - 30.0 °C |
68.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 143 µm/m-°C @Temperature -30.0 - 30.0 °C |
79.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 51.0 °C @Thickness 3.20 mm |
124 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 42.0 °C @Thickness 3.20 mm |
108 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics ULTEM LTX300A PEI Copolymer
- SABIC Innovative Plastics Noryl N1150 PPE+HIPS (Asia Pacific)
- Unitika elitel UE3201 Polyester, Pellet
- Chosun Refractories BTB-17 Casting Block
- Dow R792-35RNA Polypropylene Random Copolymer Resin
- 3M 5650 Silicone Rubber Termination Kits
- 3M 7244 HP Indigo Optimized Polyester Label Product
- Adamas Adalon® 600 PTFE, Boro Nitruro
- Permabond A134 Anaerobic Retainer
Copyright © lookpolymers.com All Rights Reserved