LyondellBasell Lupolen® 5261 Z HDPE, Blow Molding Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade |
| Manufacturer | LyondellBasell |
| Trade Name | Lupolen® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Lupolen® 5261 Z HDPE, Blow Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Relatively high viscosity blow molding grade for rigid, stackable and highly shock resistant containers for packaging all types of hazardous materials such as flammable, corrosive, poisonous and surface-active chemicals.Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | |
| Water Absorption | 0.010 % | 0.010 % | |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | |
| High Load Melt Index | 0.10 g/10 min @Load 21.6 kg, Temperature 190 °C |
0.10 g/10 min @Load 47.6 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 9.0 % | 9.0 % | |
| Tensile Modulus | 1.20 GPa | 174 ksi | |
| Tensile Impact Strength | 300 kJ/m² | 143 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 430 MPa | 62400 psi | |
| Tensile Creep Modulus, 1000 hours | 290 MPa | 42100 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 145 µm/m-°C @Temperature 20.0 °C |
80.6 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 134 °C | 273 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | |
| Vicat Softening Point | 80.0 °C | 176 °F | |
| Flammability, UL94 | HB @Thickness 0.400 mm |
HB @Thickness 0.0157 in |
|
| Oxygen Index | 17 % | 17 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.4 @Frequency 100 Hz |
2.4 @Frequency 100 Hz |
|
| 2.4 @Frequency 1e+6 Hz |
2.4 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 150 kV/mm | 3810 kV/in | |
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
|
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Nye Lubricants 774F-1 (NG) Synthetic Oil
- Solvay Engineered Polymers SEQUEL® 2330 Engineered Polyolefin (discontinued **)
- SABIC Innovative Plastics NORYL WCD795 PPE-TPE (Asia Pacific)
- Sharadaa Ceramics HH 40SD Normal Medium and High Heat and Super Duty Brick
- Samsung Cheil Industries Starex® VB-4921 ABS, Glass Filled FR
- Styron Magnumâ„¢ 8391 MED Acrylonitrile Butadiene Styrene (ABS) Resin
- Shin-Etsu Silicones KSG-43 Fluid
- Borealis BS2581 High Density Polyethylene for Blow Molding
- Carpenter AerMet® 340
- ExxonMobil Santoprene® 201-55W175 Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved