SABIC Innovative Plastics LNP Stat-kon FX97333 PE
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon FX97333 PE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* FX97333 is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ISO 1183 |
| 0.994 g/cc | 0.0359 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.99 % | 0.99 % | 23°C / 50% RH; ISO 62 |
| 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 527 |
| 20.0 MPa | 2900 psi | ASTM D 638 | |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527 |
| 20.0 MPa | 2900 psi | ASTM D 638 | |
| Elongation at Break | 71.2 % | 71.2 % | ISO 527 |
| 98.2 % | 98.2 % | ASTM D 638 | |
| Elongation at Yield | 17.6 % | 17.6 % | ASTM D 638 |
| 19.6 % | 19.6 % | ISO 527 | |
| Tensile Modulus | 0.660 GPa | 95.7 ksi | 1 mm/min; ISO 527 |
| 0.810 GPa | 117 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 19.0 MPa | 2760 psi | ASTM D 790 |
| Flexural Modulus | 0.630 GPa | 91.4 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.900 J/cm @Temperature 23.0 °C |
1.69 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 96.0 kJ/m² @Temperature 23.0 °C |
45.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 70.0 J | 51.6 ft-lb | Multiaxial Impact; ISO 6603 |
| 30.0 J @Temperature 23.0 °C |
22.1 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 44.0 °C @Thickness 3.20 mm |
111 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 ohm-cm - 1e+05 | 100 ohm-cm - 1e+05 | ASTM D 257 |
| Surface Resistance | 100 ohm - 1e+05 | 100 ohm - 1e+05 | ASTM D 257 |
Users viewing this material also viewed the following:
- Nye Lubricants 732C-1 (IG) Synthetic Oil
- LATI LASTIROL R G/30 30% Glass Fiber Reinforced Polystyrene (PS) (discontinued **)
- Mallard Creek Polymers ROVENE® 4150 SBR Latex
- Polyplastics Duranex® 3105 Polybutylene Terephthalate (PBT), Standard, 15% GF filled
- Polyram PlusTek PA301G2 Nylon 6.6 for Injection Molding, 10% Glass Fiber Reinforced, Heat Stabilized
- ExxonMobil Teresstic M Series 32LT
- Carmel Olefins IPETHENE® 213 Low Density Polyethylene
- A. Schulman ComAlloy Hiloy® 636 Nylon 6/6, Glass/Mineral Reinforced, Flow Enhanced
- DuPont Teijin Films Mylar® LBT-2 Polyester Packaging Film, 75 Gauge
Copyright © lookpolymers.com All Rights Reserved