- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 193 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 193 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| Niche Polymer PA6GF13N Nylon 6, 13% Glass Fiber Filled Information provided by Niche Polymer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| Polymer Resources NY66-M40-[color]-H Nylon 66, 40% Mineral Filled, Heat Stabilized Nylon 66, 40% Mineral Filled, Lubricated, Heat StabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N1040ML Nylon 6/6 (DAM)
(discontinued **) Information provided by Ravago. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C @Thickness 3.20 mm |
379 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP EL002 PEI LNP* Lubricomp* EL002 is a compound based on Polyetherimide resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP RAL22S PA 66 (Asia Pacific) LNP* Lubricomp* RAL22S is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Ultem 1010K PEI (Europe-Africa-Middle East) Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 GF20 IM2 BK 20% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impac.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics ULTEM HU1010 PEI Transparent, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI),.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® TPX-PBT-00014 40% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 40% Filler by WeightFeatures: Flame RetardantUL File Number: E157318Information provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C @Thickness 6.40 mm |
379 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 830 PBT 30% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics ULTEM AUT200 PEI Transparent high flow Polyetherimide (Tg 217C). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C @Thickness 3.20 mm |
379 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOTUF V1000SU PA LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C @Thickness 3.20 mm |
379 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl GTX GTX4110 PPE+PA66 Non-brominated, non-chorinated Flame Retardant PPE/PA66 alloy, 10% glass reinforced. Combines ductility, modulus and high CTI with dimensional stability.This data was supplied by SABIC-IP for the A.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF15 15% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | ASTM D648 |
| Plenco 3509 Phenolic, Granular, Transfer Molded PLENCO 03509 is a mineral and flock filled phenolic molding compound offering excellent electrical properties, dimensional stability, and improved heat resistance. UL recognized under component file.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF15 15% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF15 15% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | ASTM Test |
| BASF Ultramid® 8262G HS BK-102 7/13% Glass/Mineral Filled PA6 (Dry) Ultramid 8262G HS BK-102 is a heat stabilized, pigmented black, 20% glass and mineral reinforced PA6 injection molding compound resulting in a balance of engineering properties with excellent dimens.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | ASTM D648 |
| Ashley Polymers Ashlene® P124WO PBT Polyester, 20% Glass Reinforced Flame retardant 20% glass reinforced, natural. Colors will modify properties.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | ASTM Test |
| BASF Ultramid® B3ZG3 15% Glass Filled PA6 (Dry) Ultramid B3ZG3 is an impact-modified, 15% glass fiber reinforced injection molding PA6 grade. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON QEL329 PA 6/10 LNP STAT-KON* QEL329 is a compound based on Nylon 6/10 resin containing 10% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant, Flame Retardant.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C @Thickness 3.20 mm |
379 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermotuf V1000SU PA LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C @Thickness 3.20 mm |
379 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOTUF V1000SU PA (Asia Pacific) LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized. |
|||