SABIC Innovative Plastics LNP THERMOTUF V1000SU PA (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF V1000SU PA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.600 % | 0.600 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.021 - 0.023 cm/cm @Time 86400 sec |
0.021 - 0.023 in/in @Time 24.0 hour |
ASTM D955 |
| 0.022 cm/cm @Time 86400 sec |
0.022 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.025 - 0.027 cm/cm @Time 86400 sec |
0.025 - 0.027 in/in @Time 24.0 hour |
ASTM D955 |
| 0.026 cm/cm @Time 86400 sec |
0.026 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 53.0 MPa | 7690 psi | ISO 178 |
| 55.0 MPa | 7980 psi | ASTM D790 | |
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
| 2.06 GPa | 299 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.97 J/cm | 3.69 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 134 µm/m-°C @Temperature -40.0 - 40.0 °C |
74.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 135 µm/m-°C @Temperature -40.0 - 40.0 °C |
75.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 133 µm/m-°C @Temperature -40.0 - 40.0 °C |
73.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 134 µm/m-°C @Temperature -40.0 - 40.0 °C |
74.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 192 °C @Thickness 3.20 mm |
378 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 193 °C @Thickness 3.20 mm |
379 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 728J (RL) Synthetic Oil
- ExxonMobil Santoprene® 261-87 Thermoplastic Elastomer (discontinued **)
- SABIC Innovative Plastics Lexan® HPH4404 PPC+PC
- Momentive Performance Materials RTV128 Translucent Adhesive Sealant, General Purpose Paste
- Lehmann & Voss LUVOCOM® 1-0867 Polyamide 66, with aramid reinforcement and PTFE, lubricant modified, heat stabilized
- Solvay TECHNYL® eXten D247 F Nylon 66 & 610
- Fainplast Compounds PH 65/A Flexible PVC, Transparent Extrusion
- Arkema Group Rilsan® AESN P302 TL Nylon 12, Flexible Tubing Grade (Conditioned)
- Buckeye Polymers BP RPP 3019 TU Polypropylene, 30% Mineral Filled
- Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 2 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness