- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 165 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 165 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75, ASTM D648 |
| Nilit Nilamon A3 H K8 40% Mineral Reinforced PA66 Description: Nilamon A3 H K8 combines good stiffness with low warpage. It is used for applications which need a degree of rigidity, particularly at higher temperatures, but which need to stay flat a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT4141 PC Copolymer XHT4141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP KONDUIT PX08322 PA 6 (Europe-Africa-Middle East) Thermally conductive mineral filled PA6 non-halogen FR compound |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT4141 PC Copolymer (Asia Pacific) XHT4141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 - 238 °C | 329 - 460 °F | Average value: 189 °C Grade Count:9 |
| Overview of materials for Phenolic, Novolac, Cellulose Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Cellulose Filled". Each property range of values reported is minimum and maximum valu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 6.40 mm |
329 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUCEL GC240 POM+GF40%, High Rigidity Feature: Injection Molding, POM+GF40%, High RigidityApplication: Casings of Pump and Pivot BearingsCAS No. 66455-31-0 and 65997-17-3Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1, -2 |
| Lanxess Durethan® DP BKV 30 XF 000000 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, injection molding, improved flowability, improved surface finishInformation provided by LANXESS. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | |
| LATI Lasulf PSU Polysulfone (PSU). Unfilled. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformati.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | |
| LATI Latilub 82-05GR G/30 PA12, 30% Glass Fiber Reinforced, Graphite Filled Self-lubricating product based on Polyamide 12 (PA12). Graphite. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 6.40 mm |
329 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 1285 PEI (Asia Pacific) Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact compliant in recognized colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP PH1000A PA 6 LNP THERMOCOMP* PH1000A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | As Molded; ASTM D648A |
| Sumitomo Bakelite North America RX® 525 Cellulose Reinforced Phenolic Novolac RX 525 is a cellulose fiber reinforced phenolic novolac molding compound. This material is recommended for parts requiring moderate toughness. It is designed to meet the requirements of ASTM D-594.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL HH180 PPE+PS Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics NORYL HH180 PPE+PS (Asia Pacific) Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | As Molded; ASTM D648A |
| Sumitomo Bakelite North America Epiall® 2061B-1 Mineral and Glass Filled Electrical Encapsulation Grade Epoxy Epiall 2061B-1 is a fiberglass and mineral reinforced epoxy molding compound, with excellent dimensional stability, good electrical insulation properties, and good strength.Information provided by S.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ASTM D648 |
| Plenco 2369 Phenolic, Granular, Injection Molded PLENCO 02369 is a general purpose, organic filled phenolic molding compound, formulated to minimize the generation of free ammonia for applications that are sensitive to such formation. PLENCO 02369.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | 0.5 inch; ASTM D648 |
| PlastxWorld CEVIAN® A2604 20% GF PA/ABS Alloy, DAM Property data is for dry as molded (DAM) samples.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ASTM D648 |
| Unitika PT-3020 Characteristics: Dimensional accuracy (planarity) Heat resistance Creep resistance and elasticity RigidityInformation provided by Unitika Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® 1SBVX-30H LDS black PA1010-GF30 Product Description: Grilamid 1SBVX-30H LDS black is a 30% glass fiber reinforced Polyamide 1010 injection molding grade. This grade is specifically optimized for the laser Direct Structuring techno.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® LV-50H FWA black 9225 PA12-GF50 Product description: Grilamid LV-50H FWA black 9225 is a 50 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combine.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® LV-5H PA12-GF50 Product description: Grilamid LV-5H is a 50% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following product profile: very low water absorptionhigh dimensiona.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® XE 3915 PA12-GF50 Product description: Grilamid XE 3915 is a 50% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following produce profile:Good UV StabilityHigh impact strengthVe.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Eurostar Staramide BT6 PA6, 30% Mineral Filled, Injection Molded Staramide BT6 is a 30% Mineral Filled, Polyamide 6, Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ASTM D648 |
| E-Polymers SEPAZ® LC50 PP Copolymer LFT Resin Long Fiber Thermoplastics: SEPAZ LFT products, injection moldable long fiber-reinforced thermoplastics (LFT), are made using a unique pultrusion that thoroughly wets out the glass fibers and deliver.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | |
| Arkema Group Rilsan® AZM 30 GT8LD Nylon 12, 30% Glass Fiber Filled (Conditioned) Designation ISO 1874-PA12,MHLS,16-050,(G+C)(F+D)(30+05)Rigid grade with glass fiber (30%) and graphite filler for injection molding. Available color: steel black gray. Reinforced light and heat stab.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | injection molded unannealed; ASTM D-648-95 |
| Multibase Multi-ABS 3245 FR Flame Retardant ABS Data provided by Multibase. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | |
| LATI Latilub 88/10-10T Y/10 PEEK, 10% Aramid Fiber Reinforced, PTFE Filled Self-lubricating product based on Polyetheretherketone (PEEK). PTFE. Aramid fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | |
| LATI Latilub 88/50-30GRT PEEK, Graphite/PTFE Filled Self-lubricating product based on Polyetheretherketone (PEEK). Graphite / PTFE.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indu.. |
|||