LATI Latilub 88/10-10T Y/10 PEEK, 10% Aramid Fiber Reinforced, PTFE Filled

Category	Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Aramid Fiber Filled
Manufacturer	LATI
Trade Name	Latilub
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 88/10-10T Y/10 PEEK, 10% Aramid Fiber Reinforced, PTFE Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Polyetheretherketone (PEEK). PTFE. Aramid fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.37 g/cc	0.0495 lb/in³
Linear Mold Shrinkage, Flow	0.0075 - 0.0115 cm/cm	0.0075 - 0.0115 in/in
Linear Mold Shrinkage, Transverse	0.0085 - 0.0125 cm/cm	0.0085 - 0.0125 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	75.0 MPa	10900 psi
Elongation at Break	6.0 %	6.0 %
Tensile Modulus	4.00 GPa	580 ksi
Charpy Impact Unnotched	5.50 J/cm²	26.2 ft-lb/in²
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²
Coefficient of Friction, Dynamic	0.20	0.20
Coefficient of Friction, Static	0.25	0.25
K (wear) Factor	6.70 x 10^-8 mm³/N-M	3.33 x 10^-10 in³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	240 °C	464 °F
Deflection Temperature at 1.8 MPa (264 psi)	165 °C	329 °F
Vicat Softening Point	285 °C @Load 5.00 kg	545 °F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	360 - 390 °C	680 - 734 °F
Mold Temperature	170 - 200 °C	338 - 392 °F
Drying Temperature	120 - 150 °C @Time 10800 sec	248 - 302 °F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa