- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 145 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 145 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Ovation Polymers Optrene 10GF Polypropylene Chemically coupled glass reinforced(10%) polypropylene with high strength and HDT.Information provided by Ovation Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH GF15030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT2141 PC Copolymer XHT2141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT2141 PC Copolymer (Asia Pacific) XHT2141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT2146 PC Copolymer (Asia Pacific) XHT2146 resin is a high flow, high heat polycarbonate copolymer with improved release performance compared to Lexan* XHT2141 resin. It is available in a range of opaque and limited transparent colo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | HDT/B; ASTM D648 |
| GEHR Plastics ECOGEHR® PA 11 Nylon 11 Conditioned
(discontinued **) Nylon 11 is made 100% from the components of castor oil, and is thus wholly bio-based. ECOGEHR® Nylon 11 possesses similar properties to Nylon 12, and an excellent status with respect to applicatio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | |
| Lehmann & Voss LUVOCOM® 50-7154/V0 Polycarbonate, with carbon fiber, low-warpage Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Reduced moment of inertia compared with me.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | |
| LATI Latilub 52/30-15T G/30 PP Homopolymer, 30% Glass Fiber Reinforced Self-lubricating product based on Polypropylene homopolymer (PPh). PTFE. Glass fibersAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ASTM D648 |
| LyondellBasell Higlass BJ44A Polypropylene Copolymer, 45% Glass Fiber Key Features: medium melt flow, high modulus, chemically coupled, glass fiber-reinforced polypropylene copolymer, high stiffness, good impact strength, excellent processabilityApplications: grille o.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics NORYL V03550 PPE+HIPS Noryl* V03550 is a 35% milled fibre reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON DE003 PC (Asia Pacific) LNP STAT-KON* DE003 is a compound based on Polycarbonate resin containing Carbon Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON DEL329E PC (Asia Pacific) LNP* Stat-kon* DEL329E is a compound based on Polycarbonate resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Stat-kon DEL339XC PC LNP STAT-KON* DEL339XC is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 6.40 mm |
293 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGN2000 PC (Asia Pacific) |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP MX99432 PP LNP* THERMOCOMP* MX99432 is a compound based on Polypropylene resin containing Proprietary Filler(s). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RZ0069 PA 66 (Asia Pacific) LNP* Thermocomp* RZ0069 is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant, Milled Glass. Added features of this material include: Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Stat-kon DEL339XC PC (Asia Pacific) LNP STAT-KON* DEL339XC is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.This data was supp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP MF004AS PP LNP THERMOCOMP* MF004AS is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP MF004S PP LNP THERMOCOMP* MF004S is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | 0.25 inch; ASTM D648 |
| PlastxWorld CEVIAN® B6526 30% GF PBT/ABS Alloy Glass fiber and mineral filled, low warpage and flame retarded PBT/ABS.Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | DIN 53461 |
| Polyram RamOfin PPH300G6 Polypropylene, 30% Glass Fiber 30% glass fiber reinforced polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ASTM D648, ISO 75 |
| EPICHEM Epilon PC GF 10 V0 Polycarbonate, 10% Glass Fiber Characteristics: self-extinguishing V0 at 1,6 mm, 10% glass fibre filled |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Eurostar Starflam AFR682A1 PA66, Mineral Reinforced, Flame Retardant, Injection Molding Starflam AFR682A1 is a Flame Retardant, Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ISO 75 |
| Eurotec® Tecolen® HP30 KG30 NL HS 0B PPCP, 30% glass fiber/glass bead reinforced, heat stabilized, natural Information provided by Eurotec® |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | HDT/B; ASTM D648 |
| GEHR Plastics ECOGEHR® PA 11 Nylon 11 Dry
(discontinued **) Nylon 11 is made 100% from the components of castor oil, and is thus wholly bio-based. ECOGEHR® Nylon 11 possesses similar properties to Nylon 12, and an excellent status with respect to applicatio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylex® P1010G15 HB Polycarbonate, 15% Fiberglass Reinforced Information provided by Ravago. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP DFL36HL PC LNP LUBRICOMP* DFL36HL is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractable, Healthcare. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | |
| LATI Latimass 62-01 D025 PA6 Specific density compound based on Polyamide 6 (PA6). Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Ter.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP PH0800A PA 6 LNP* THERMOCOMP* PH0800A is a compound based on Nylon 6 resin. Added feature of this material is: High Specific Gravity. |
|||