SABIC Innovative Plastics LNP STAT-KON DE003 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DE003 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DE003 is a compound based on Polycarbonate resin containing Carbon Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.160 % | 0.160 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00040 - 0.0010 cm/cm @Time 86400 sec |
0.00040 - 0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.00040 - 0.0013 cm/cm @Time 86400 sec |
0.00040 - 0.0013 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0040 cm/cm @Time 86400 sec |
0.0030 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0032 - 0.0041 cm/cm @Time 86400 sec |
0.0032 - 0.0041 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 108 MPa | 15700 psi | ISO 527 |
| 109 MPa | 15800 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.1 % | 2.1 % | ASTM D638 | |
| Tensile Modulus | 8.41 GPa | 1220 ksi | 1 mm/min; ISO 527 |
| 8.78 GPa | 1270 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 176 MPa | 25500 psi | ISO 178 |
| 182 MPa | 26400 psi | ASTM D790 | |
| Flexural Modulus | 7.79 GPa | 1130 ksi | ASTM D790 |
| 8.04 GPa | 1170 ksi | ISO 178 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.91 J/cm | 9.20 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J | 11.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 17.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.78 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 17.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.83 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 ohm - 1e+05 | 10 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8322 (857A) (UF) Synthetic Oil
- Objet FullCure® 830 Vero White Resin for Rapid Prototyping
- PTS Tristar® PC-10FR-(V18) 18 MFI Flame Retardant, UV Stabilized Polycarbonate With Release
- Kolon Kocetal® DP301 Modified Grade Acetal Copolymer (discontinued **)
- Greene Tweed CHEMRAZ® E38 Perfluoroelastomer
- Haynes 556® alloy, 50% cold reduction
- Sylvin Technologies 9999-80 Natural PVC Molding Compound
- SABIC Innovative Plastics NORYL GTX APS440 PPE+PPS (Asia Pacific)
- A. Schulman POLYFLAM™ RCP 770C/CW
- AIM 100In Solder for Photonic Packaging
Copyright © lookpolymers.com All Rights Reserved