Barlog Plastics KEBAFORM C 520.0 POM Copolymer unreinforced
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBAFORM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBAFORM C 520.0 POM Copolymer unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
POMInformation provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.22 % | 0.22 % | similar to ISO 62 test |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | ISO 294-4 |
| Melt Flow | 45 g/10 min @Load 2.16 kg, Temperature 190 °C |
45 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | ISO 527-1 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO 527-1 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527-1 |
| Charpy Impact Unnotched | NB | NB | ISO 179-1eU |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 166 °C | 331 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | POM |
Users viewing this material also viewed the following:
- Nabaltec APYMAG® 40 Magnesium Hydroxide
- Polymax® Maxelast® P3850 TPE, PP Overmold or Standalone use
- Polykemi AB POLYlux 4010 MP PC/PBT-Blend
- Lehmann & Voss LUVOCOM® 1-7139 Polyamide 66, with aramid reinforcement and PTFE, heat stabilized
- Heatbath/Park Wire Annealing Quenching and Tempering Salt
- Westlake EMAC® Plus SP1358 21.5% Ethylene-Methyl Acrylate Copolymer
- Williams Advanced Alloys WS200 Solder
- CLAL-MSX SICLANIC S® TF Quenched Copper Alloy, precipitation treated
- Austin Novel Materials Texalan® 582A Polyether-based TPU
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 25A, Non-Black Sulfur Cure
Copyright © lookpolymers.com All Rights Reserved