- Polyram RamSter PF701 PBT, UV Stabilized
Polyram RamSter PF701 PBT, UV Stabilized
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamSter PF701 PBT, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UV stabilized high viscosity PBT for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | DIN 53479 |
| Water Absorption | 0.60 % | 0.60 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23° C, 50% RH; DIN 53714 |
| Linear Mold Shrinkage | 0.021 cm/cm | 0.021 in/in | |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 250 °C |
25 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ASTM-D638 |
| Elongation at Break | 60 % | 60 % | ASTM-D638 |
| Flexural Strength | 95.0 MPa | 13800 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.500 J/cm @Temperature 23.0 °C |
0.937 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Glow Wire Test | 750 °C | 1380 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | DIN 53482 |
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP Faradex NS0039 PC/ABS (Europe-Africa-Middle East)
- Indium Corp. Indalloy 160-190 Fusible Bismuth Alloy
- EMS-Grivory Grivory® L 20 H FR PA12 FR
- DuPont Performance Polymers Delrin® 570 NC000 Acetal (POM) (Unverified Data**)
- ChevronTexaco Bright-Cut® AXH Metal Working Fluid
- Axiall 898 Wire & Cable Flexible PVC
- AK Steel Cold Rolled Carbon Steel, Bake Hardenable (BH 180), SAE J2340 Type 180 B
- LNP ULTEM® SMU5852 Polyetherimide, 30% Carbon Fiber Reinforcement, 15% PTFE Lubricant (discontinued **)
- Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened
Copyright © lookpolymers.com All Rights Reserved