- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 311 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 311 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH GF8030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Lexan® XHT2141 PC Copolymer (Europe-Africa-Middle East) XHT2141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C @Thickness 3.20 mm |
311 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT2143 PC Copolymer (Europe-Africa-Middle East) XHT2143 is a high flow, UV stabilized, high heat polycarbonate copolymer with an HDT/Af of 142 C. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | DIN 53461; ASTM D648 |
| Kolon SPESIN® KP210 General Purpose PBT Resin
(discontinued **) SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High hea.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C @Thickness 3.20 mm |
311 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT2146 PC Copolymer (Asia Pacific) XHT2146 resin is a high flow, high heat polycarbonate copolymer with improved release performance compared to Lexan* XHT2141 resin. It is available in a range of opaque and limited transparent colo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Kolon SPESIN® KP270 General Purpose PBT Base Resin Excellent extrudabilityApplications: CablesInformation provided by API-Kolon. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D1525, HDT Method B |
| Loxim 300 00HB Nylon 6 Information provided by Loxim Industries |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Gromax PBT 1100-211XG Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Gromax PBT 1200-211L Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | |
| LATI Latan 9 POM Polyoxymethylene (POM). Unfilled. Medium viscosity. Very good tribological properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by La.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | |
| LATI Latene® AG3H2W G/30-V0E PP Homopolymer, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Metal stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE freeAvailability: A.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | |
| LATI Latilub 62-15ST PA6 Self-lubricating product based on Polyamide 6 (PA6). Silicone / PTFE.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Term.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | |
| LATI Latimass 82-03 D080 PA12 Specific density compound based on Polyamide 12 (PA12). Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria T.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL V02570 PPE+HIPS (Asia Pacific) Noryl* V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP LL002 PEEK LNP* LUBRICOMP* LL002 is a compound based on Polyetheretherketone containing 10% PTFE. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Samyang Tribit® 1700 PBT, Middle Viscosity Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1700 is a middle viscosity grade.Informatio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C @Thickness 3.20 mm |
311 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL N300X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP (Europe-Africa-Middle East) PPX630 is a 30% glass filled alloy of PP and PPO providing design freedom for applications requiring a wide range of stiffness, toughness and temperature. Generic identification acc. ISO11469: PP+PP.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1236 Glass Filled Chemically Coupled Homopolymer Polypropylene DescriptionPolyfort® FPP 1236 is a 20% glass filled chemically coupled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1606 Glass Filled Chemically Coupled Impact Copolymer Polypropylene DescriptionPolyfort® FPP 1606 is a 30% glass filled chemically coupled impact copolymer polypropylene product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 3710 Glass Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 3710 is a 45% glass filled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1606 Glass Filled Chemically Coupled Impact Copolymer Polypropylene DescriptionPolyfort® FPP 1606 is a 30% glass filled chemically coupled impact copolymer polypropylene product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1239H Glass Filled Chemically Coupled Homopolymer Polypropylene DescriptionPolyfort® FPP 1239H is a 30% glass filled chemically coupled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1236 Glass Filled Chemically Coupled Homopolymer Polypropylene DescriptionPolyfort® FPP 1236 is a 20% glass filled chemically coupled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 3710 Glass Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 3710 is a 45% glass filled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0339G25M5CL Glass/Mineral Reinforced Coupled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | |
| Arkema Group Rilsan® AUM 30 T6LD Nylon 12, 30% Glass Bead Filled (Conditioned) Designation ISO 1874-PA12,MHLR,16-020,GB30Rigid grad with glass beads filler (30%) for injection molding. Available colors: black and natural. Light and heat stabilized. Mold-release agent.Reinforce.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 - 260 °C | 311 - 500 °F | Average value: 223 °C Grade Count:50 |
| Overview of materials for Nylon 66, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, PTFE Filled". Each property range of values reported is minimum and maximum values of appropri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C @Thickness 3.20 mm |
311 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOL GP2300 PP+GF30% Description: Injection Molding, PP+GF30%, General PurposeApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0 and 65997-17-3Information provided by LG Chemical |
|||