LATI Latilub 62-15ST PA6

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	LATI
Trade Name	Latilub
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 62-15ST PA6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Polyamide 6 (PA6). Silicone / PTFE.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.20 g/cc	0.0434 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0090 - 0.012 cm/cm	0.0090 - 0.012 in/in
Linear Mold Shrinkage, Transverse	0.0095 - 0.013 cm/cm	0.0095 - 0.013 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	55.0 MPa	7980 psi
Elongation at Break	45 %	45 %
Elongation at Yield	5.0 %	5.0 %
Tensile Modulus	2.40 GPa	348 ksi
Charpy Impact Unnotched	NB	NB
Charpy Impact, Notched	0.500 J/cmÂ²	2.38 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.16	0.16
Coefficient of Friction, Static	0.21	0.21
K (wear) Factor	8.10 x 10^-8 mmÂ³/N-M	4.02 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	155 Â°C	311 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	55.0 Â°C	131 Â°F
Vicat Softening Point	200 Â°C @Load 5.00 kg	392 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	230 - 250 Â°C	446 - 482 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	90.0 - 100 Â°C @Time 10800 sec	194 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa