Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 252 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycoloy® CX5640 PC+ABS (Europe-Africa-Middle East) Cycoloy* CX5640 is a all purpose PC+ABS blend specially developed for applications requiring weld line strength. High heat resistance combined with good flow, excellent impact and low temperature du.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPC TS4030 H Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Cycoloy® HC1204HF PC+ABS High heat PC/ABS blend offering good flow and excellent impact. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® HCX1640 PC+ABS (Europe-Africa-Middle East) CYCOLOY™ HCX1640 a PC+ABS blend specially developed for medical devices and pharmaceutical applications requiring improved mechanical performance . It combines good flow with excellent impact and l.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH TS15040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| PolyMirae Moplen HP640N Injection Molding Grade Polypropylene Moplen HP640N is the polypropylene homopolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen HP640N is a homopolymer particularly suitable for injection molding.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HPF1 PC Copolymer 25 MFR LEXAN High Flow Ductile Copolymer Healthcare Grade |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH T4030 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C @Thickness 6.40 mm |
252 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa JE2-R2G20 Glass Fiber Reinforced ABS/PBT Alloy Features:High stiffness, high hardnessGood mechanical strengthGood chemical resistanceGood size stabilityGood heat stabilityLow tendency to warpApplications:Optical appliance (camera, video)Sports a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Valox® IQ357U PBT+PC (Asia Pacific) Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xylex HX7409HP PC+POLYESTER (Europe-Africa-Middle East) Low flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change (MoC), biocompatible (ISO 10993 or USP Class VI).. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ISO 75 |
| Teijin Multilon DN-1520B Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 20 % filler. Improved stiffness and high fluidity realizes a thin wall.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP MF002AS PP LNP THERMOCOMP* MF002AS is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP MH0500C PP LNP* THERMOCOMP* MH0500C is a compound based on Polypropylene resin. Added feature of this material is: High Specific Gravity. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| ScanTube PTFE Tubing Information provided by ScanTube, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL PX0844 PPE+PS PPE+PS blend. Unfilled. UL94 HB rated. Low water absorption. Hydrolytic stability. Dimensional stability. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ISO 75-2 |
| Borealis Bormed™ HF855MO Polypropylene Homopolymer for Medical Applications Bormed HF855MO is a high modulus polypropylene homopolymer and is especially developed within the proprietary Borstar technology. Bormed HF855MO combines an unique balance of properties for high sp.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| TPI Porene® ABS-KU650 Super High Heat ABS Resin Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C @Thickness 3.17 mm |
252 °F @Thickness 0.125 in |
ISO 75 |
| A. Schulman FORMION™ FI 233 15% Mineral Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 233 is an injection molding grade, 15% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance and high stiffness. A.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ISO 75-1/-2 |
| Covestro Bayblend® T65 Polycarbonate + ABS General purpose injection molding gradeVicat/B 120 temperature = 120 °Cgood low temperature impact strengthPreprocessingMax. Water content |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0334T20L1 Talc Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 246 SAN, Glass/Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0339T20L1 Talc Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH T8030 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® ML1661 PC Copolymer (Asia Pacific) Medium-flow impact-modified light-shielding high-flow-ductile PC copolymer. Available in white color only. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Xylex HX7409HP PC+POLYESTER (Asia Pacific) Low flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change (MoC), biocompatible (ISO 10993 or USP Class VI).. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH TS2040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1731 PC Copolymer (Europe-Africa-Middle East) 25 MFR LEXAN High Flow Ductile Copolymer UV-stabilized |
|||