- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 223 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 223 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C @Thickness 3.18 mm |
223 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ MD 4245-59770 Polypropylene Copolymer (PP Copolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| SABIC PP 511A Polypropylene Homopolymer for Spunbond Applications Product Description: PP 511A is a controlled rheology grade with a narrow molecular weight distribution intended for spun bond fiber extrusion applications.PP 511A has the following features:Consis.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Unannealed (0.250 in); ASTM D648 |
| Ravago Manufacturing Americas Hysun™ 678 ASA Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families. Availibility: North America F.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hysun™ 678UV ASA Available in North America Additive: UV Stabilizer Features: Good Impact Resistance and High Heat ResistanceRoHS CompliantForm: PelletsInformation provided by Ravago |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| PolyMirae Moplen HP652P Fiber (BCF/CF) Grade Polypropylene Moplen HP652P is the polypropylene homopolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen HP652P is a homopolymer particularly suitable for heavy denier BCF .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| PolyMirae Moplen HP653P Fiber (BCF/CF) Grade Polypropylene Moplen HP653P is the polypropylene homopolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen HP653P is a homopolymer particularly suitable for heavy denier BCF .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | |
| Ineos ABS NOVODUR® KU 2-5300 ABS, Injection Grade
(discontinued **) Injection molding grade, high heat resistance and toughness, low-emission.Applications: Automotive parts, household goods.Information provided by the manufacturer.Novodur is produced by Styrolution .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Annealed, 80°C, 4 hours; ISO 75 |
| LG Chemical LG-703A ABS, Low Gloss, General Purpose Information Provided by LG Chem |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Unannealed; ASTM D648 |
| Global PP-2540-K Polypropylene Block Copolymer Description-opacity, medium to high stiffness, high impact strength at low temperatureApplications-paint drum, storage & transport containerInformation provided by Global Polymers Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| IRPC Polimaxx Polene 2541TC Polypropylene Block Copolymer CHARACTERISTICS: EXCELLENT FLOWABILITY, HIGH STIFFNESS, HEAT STABILITY, HIGH IMPACTAPPLICATIONS: INJECTION MOLDING SPECIALLY FOR WASHING TUB, ELECTRICAL APPLIANCES, THIN WALL CONTAINERS |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75B |
| Lucite International Diakon® CMH454L Acrylic Polymer Information provided by Lucite International |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75B |
| Lucite International Diakon® MH254 Acrylic Bead Polymer, High Transparency PMMA beads offer an exceptional transmission level of 92.5%, an increase of +0.5% in light transmission vs. granular grades - ideal for medical diagnostic devices.Information provided by Lucite Inte.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® ASA FR-2 WT Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Flame Retardant and Good UV ResistanceAppearance: WhiteInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | annealed; ASTM Test |
| Styrolution Luran® S 778 T ASA Luran S 778 T is an injection molding ASA grade with enhanced toughness and heat resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75-1/-2 |
| Styrolution Luran® S 778 TE Black 25991 ASA Description: Extrusion grade with enhanced toughness and heat distortion resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C @Thickness 6.40 mm |
223 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® GR-4010 ABS, 10% Glass Filled Material with 10% GF reinforcement with high stiffness that can be used in refrigerator vegetable boxesInformation provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Xenoy® X6320 PBT+PC (Asia Pacific) X6320 is a mineral filled PBT/PC resin developed for automotive painted doorhandles. Key advantages are excellent surface finish, easy processing and paint quality. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Annealed; ASTM D648 |
| Techmer ES Plastiblend® ABS HH BK MB Availability: North AmericaForms: PelletsFeatures: High Gloss and High Heat ResistanceAppearance: BlackProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C @Thickness 3.17 mm |
223 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Chase Plastics CP Pryme® A100HH ABS Molding Resin, High Heat Information provided by Chase Plastics. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | 120°C per hour; ISO 752 |
| Total PPH 4070 Polypropylene Homopolymer Polypropylene PPH 4070 is a homopolymer polypropylene with a Melt Flow index of 3 g/10 min.Polypropylene PPH 4070 has been designed for the production of BOPP film with the tenter frame process and .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer DescriptionPolypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with relatively high stiffness. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | 0.25 inch; ASTM D648 |
| PlastxWorld CEVIAN® B14E0 PBT/ABS Alloy Excellent flowability, high impact strength and toughness. These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer DescriptionPolypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with relatively high stiffness. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75-1/-2 |
| Covestro Bayblend® FR 3030 Polycarbonate + ABS, Flame Retardant Grade Flame retardant extrusion gradeVicat/B 120 temperature = 115 °Cgood extrusion and vacuum-forming behaviourUL-listing 94 V-0 (1.5 mm)halogen-free according to DIN VDE 0472-815glow wire temperature (.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| Arkema Group Pebax® 7233 Polyether Block Amide (PEBA) Information provided by Arkema Group |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | |
| Arkema Group Pebax® 7233 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) hardness 72 shore D Highest modulus PEBAX Applications: medical, extrusion SportISO data provided by the manufacturer, Arkema. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0336M10L Mica Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 213 Polystyrene, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0339W10L Wollastonite Reinforced |
|||