A. Schulman ComAlloy Hiloy® 213 Polystyrene, Glass Reinforced
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Glass Filled |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 213 Polystyrene, Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.83 J/cm | 5.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 216 - 241 °C | 421 - 466 °F |
Users viewing this material also viewed the following:
- PolyOne Stat-Tech™ AS-08CF/000 Acrylonitrile Butadiene Styrene (ABS)
- Polymax® Maxelast® F02-139A TPE, Halogen Free Extrusion Grade
- PolyOne Edgetek® QT020GFS/000 FR NATURAL - OBSOLETE Syndiotactic Polystyrene (SPS)
- Kazanorgsintez 107-278 Low Density Polyethylene Composition with Improved Processibility
- Global GA-3750 High Density Polyethylene, Film Extrusion Grade
- H.C. Starck Amperit® 516.074 Tungsten Carbide - Cobalt (WC-Co) 88-12
- H.C. Starck Pure Molybdenum PSB, Powder Metallurgy Billet
- Solvay Chemicals NOCOLOK® Sil Flux (extra fine grade) plus Binder Mixture
- SABIC Innovative Plastics LNP Stat-kon ZE0039 MODIFIED POYPHENYLENE (Asia Pacific)
- Overview of materials for Polyphenylene Ether + Styrene-Butadiene Blend
Copyright © lookpolymers.com All Rights Reserved