Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ASTM D648 |
Mytex Polymers AN18KW-01 FK Polypropylene, Rubber modified Description: Rubber modified polypropylene produced for automotive interior applications using Mytex® Technology. Specifically designed to achieve ductile performance at cold temperatures during a.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 - 67.0 °C | 145 - 153 °F | ASTM D648-06 |
Proto3000 Objet RGD525 High Temperature Prototyping Polymer Information provided by Proto3000 for their protoyping engineering services. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ASTM D648 |
LyondellBasell Adsylâ„¢ 5C30F Thermoplastic Olefin Resin Primary Processing Method: Film extrusionKey Features: thermoplastic olefin resins for film extrusion, good clarity and gloss, good moisture barrier properties, very low seal initiation temperature,.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ASTM D648 |
LyondellBasell Adsylâ„¢ 5C37F Thermoplastic Olefin Resin Primary Processing Method: Film extrusionKey Features: thermoplastic olefin resins for film extrusion, good clarity and gloss, good moisture barrier properties, very low seal initiation temperature,.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ISO 75 |
LyondellBasell Hifaxâ„¢ CA45 Thermoplastic Olefin Resin Key Features: medium melt flow, medium modulus thermoplastic elastomeric olefin resin, excellent balance of properties, excellent processability, good colorability, excellent surface appearanceAppli.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 62.8 °C | 145 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® HDPE TM20 20% Talc Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 20% Filler by WeightInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 62.8 °C | 145 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® HDPE TM20 UV BK 20% Talc Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 20% Filler by WeightAdditive: UV StabilizerFeatures: Good UV ResistanceAppearance: BlackInformation provided by TP Composi.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 62.8 °C | 145 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® HDPE TM25 25% Talc Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 25% Filler by WeightInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 62.5 °C | 145 °F | |
Teknor Apex TELCAR® 1000-92 Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 62.5 °C | 145 °F | |
Teknor Apex TELCAR® 1000-92UV Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 62.8 °C | 145 °F | Unannealed; ASTM D648 |
Teknor Apex Telcar® TL-1000-92 Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Automotive Spec.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 62.8 °C | 145 °F | Unannealed; ASTM D648 |
Teknor Apex Telcar® TL-1000-92-UV Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Automotive Spec.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | |
Eastman Ecdel PCCE 9967 Copolyester Ether Elastomer ISO data as provided by the manufacturer, Eastman Chemical |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 62.8 °C | 145 °F | ASTM D648-98c |
DSM Somos® ProtoGen™ 18920 Liquid Photopolymer, UV Postcure at HOC +3 Product DescriptionDSM Somos® ProtoGen 18920 is a liquid photopolymer that produces accurate, ABS-like parts ideal for general purpose applications. ProtoGen resins are the first SL resins to demo.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 62.8 °C | 145 °F | ASTM D648 |
Aclo Accucomp Polypropylene CPO407L Copolymer |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 - 65.0 °C | 145 - 149 °F | |
C.O.I.M. EXTER S® S 105 Orthophthalic Resin Description: The Exter S product line contains a large number of unsaturated polyester resin products with an array of properties and applications.Specific Notes for ESTER S® S 105: Medium reactivi.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ASTM D648 |
ACC EP QSZ EPI Engineered Polymers Quick Set Epoxy with Zinc EP QSZ Quick Set Epoxy with Zinc, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC’s (Volatile Organic Compound), self-leveling modified epoxy. This versatile new gene.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ASTM D648 |
ACC EP QS EPI Engineered Polymers Quick Set Epoxy EP QS Quick Set Epoxy, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC, self-leveling modified epoxy. This versatile new generation epoxy displays low blush, fast cure.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ISO 75-2 |
Borealis Borsoft™ SG220MO Polypropylene Random Copolymer for Injection Molding Borsoft™ SG220MO is a polypropylene characterized by good flow, high impact and good transparency. This grade contains antistatic and demolding additives which, together with enhanced nucleation, .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP LUBRICOMP FP003 PE (Europe-Africa-Middle East) LNP *Lubricomp* FP003 is a compound based on Polyethylene resin, containing PTFE and Silicone. Added features include: Internally Lubricated. |