SABIC Innovative Plastics LNP LUBRICOMP FP003 PE (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP FP003 PE (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP *Lubricomp* FP003 is a compound based on Polyethylene resin, containing PTFE and Silicone. Added features include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.030 cm/cm
0.030 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 12.0 MPa
1740 psi
50 mm/min; ISO 527
Tensile Strength, Yield 20.0 MPa
2900 psi
50 mm/min; ISO 527
Elongation at Break 12 %
12 %
50 mm/min; ISO 527
Elongation at Yield 9.0 %
9.0 %
50 mm/min; ISO 527
Tensile Modulus 0.900 GPa
131 ksi
1 mm/min; ISO 527
Flexural Yield Strength 18.0 MPa
2610 psi
2 mm/min; ISO 178
Flexural Modulus 0.700 GPa
102 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 80.0 kJ/m²
38.1 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 144 µm/m-°C

@Temperature 23.0 - 60.0 °C
 80.0 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 124 µm/m-°C

@Temperature 23.0 - 60.0 °C
 68.9 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C
145 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 47.0 °C
117 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af