Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
Manufacturer | Teknor Apex Company |
Trade Name | TELCAR® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Teknor Apex TELCAR® 1000-92 Thermoplastic Elastomer.pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.920 g/cc | 0.920 g/cc | +/- 0.02; ASTM D792 |
Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | 24 hours; ASTM D955 |
0.013 cm/cm | 0.013 in/in | After 30 min. at 180°F; ASTM D955 | |
Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore D | 42 | 42 | 10 second delay. +/- 3; ASTM D2240 |
Tensile Strength at Break | 7.58 MPa | 1100 psi | 20"/min Type 1; ASTM D412 |
Tensile Strength, Yield | 10.3 MPa | 1490 psi | ASTM D412 |
10.992 MPa | 1594.3 psi | 107% Retention, Air Oven Aged 42 days at 121°C | |
11.30 MPa | 1639 psi | 110% Retention, Air Oven Aged 42 days at 110°C | |
Elongation at Break | 140 % | 140 % | |
181.5 % | 181.5 % | 33% Retention, Air Oven Aged 42 days at 110°C | |
203.5 % | 203.5 % | 37% Retention, Air Oven Aged 42 days at 121°C | |
550 % | 550 % | ASTM D412 | |
Elongation at Yield | 16 % | 16 % | ASTM D412 |
100% Modulus | 0.00841 GPa | 1.22 ksi | ASTM D412 |
300% Modulus | 0.008522 GPa | 1.236 ksi | ASTM D412 |
Flexural Modulus | 0.2899 GPa | 42.05 ksi | ASTM D790 |
Izod Impact, Notched | NB | NB | Heat Aging Performance 1000 hrs at 120°C |
NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
Heat Aging Performance 1000 hrs at 120°C | |
Gardner Impact | 33.9 J @Temperature -30.0 °C |
25.0 ft-lb @Temperature -22.0 °F |
|
Tensile Impact Strength | >= 470 kJ/m² | >= 224 ft-lb/in² | |
Impact Test | 22.6 J @Temperature -40.0 °C |
16.7 ft-lb @Temperature -40.0 °F |
At Yield. Deflection: 693 mils, Force: 425 lbs (Instrumented Impact, 9000 in/min) |
39.5 J @Temperature -40.0 °C |
29.2 ft-lb @Temperature -40.0 °F |
At Break. Deflection: 1359 mils, Failure Mode: Ductile (Instrumented Impact 9000 in/min) | |
Tear Strength | 63.8 kN/m | 364 pli | Die C; ASTM D1004 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 119 µm/m-°C @Temperature -30.0 - 30.0 °C |
66.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
CTE, linear, Transverse to Flow | 117 µm/m-°C @Temperature -30.0 - 30.0 °C |
65.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
Deflection Temperature at 0.46 MPa (66 psi) | 62.5 °C | 145 °F | |
Deflection Temperature at 1.8 MPa (264 psi) | 40.7 °C | 105 °F | |
Glass Transition Temp, Tg | -55.9 °C | -68.6 °F | |
Flame Spread | 767 mm/min | 30.2 in/min | Pass: Burn Rate- Max 100; FMVSS 302 |
Descriptive Properties | Value | Comments |
---|---|---|
Fogging | 92, 3 hours at 100°C, Haake buchler |