Techmer ES HiFill® HDPE TM20 UV BK 20% Talc Filled

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer Techmer ES
Trade Name HiFill®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Techmer ES HiFill® HDPE TM20 UV BK 20% Talc Filled.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 20% Filler by WeightAdditive: UV StabilizerFeatures: Good UV ResistanceAppearance: BlackInformation provided by TP Composites, Inc.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
ASTM D792
Water Absorption 0.020 %

@Time 86400 sec
 0.020 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.020 cm/cm

@Thickness 3.17 mm
 0.020 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 50
50
ASTM D785
Tensile Strength, Yield 26.2 MPa
3800 psi
ASTM D638
Elongation at Break 15 %
15 %
ASTM D638
Flexural Strength 379 MPa
55000 psi
ASTM D790
Flexural Modulus 1.24 GPa
180 ksi
ASTM D790
Izod Impact, Notched 0.320 J/cm

@Thickness 3.17 mm
 0.600 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Izod Impact, Unnotched 3.74 J/cm

@Thickness 3.17 mm
 7.00 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 88.2 µm/m-°C
49.0 µin/in-°F
ASTM D696
Melting Point 135 °C
275 °F
Deflection Temperature at 0.46 MPa (66 psi) 62.8 °C
145 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 46.1 °C
115 °F
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Strength 22.0 kV/mm
560 kV/in
Method A (Short-Time); ASTM D149