LyondellBasell Hifaxâ„¢ CA45 Thermoplastic Olefin Resin
| Category | Polymer , Thermoplastic |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ CA45 Thermoplastic Olefin Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features: medium melt flow, medium modulus thermoplastic elastomeric olefin resin, excellent balance of properties, excellent processability, good colorability, excellent surface appearanceApplications: molded-in color automotive bumper fascias and step pads, air deflectors, appliquesDescription: Hifax CA45 medum melt flow, reactor grade thermoplastic elastomeric olefin resin has a very good balance of properties and excellent moldability. It was designed primarily for molded-in color automotive exterior components and is based on material from Montell's Spheripol process.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.890 g/cc | 0.0322 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | Tool, Montell |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ISO 868 |
| Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | ISO R527-1 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO R527-1 |
| Elongation at Break | 500 % | 500 % | ISO R527-1 |
| Elongation at Yield | 16 % | 16 % | ISO R527-1 |
| Flexural Modulus | 0.820 GPa | 119 ksi | ISO 178 |
| Izod Impact, Notched | 0.700 J/cm @Temperature -40.0 °C |
1.31 ft-lb/in @Temperature -40.0 °F |
ISO 180 |
| Impact Test | 25.0 J @Temperature -30.0 °C |
18.4 ft-lb @Temperature -22.0 °F |
MAII, E at Max Load, Ductile; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C @Temperature -30.0 - 30.0 °C |
55.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.0 °C | 109 °F | ISO 75 |
Users viewing this material also viewed the following:
- ICO Polymers ICOFLOâ„¢ 510-5018 400 Micron LDPE Powder
- Loxim 220 12HB Polybutylene Terephthalate
- SK Chemicals SKYTHANE® UB310 Co-Extruding Adhesive
- Diamond Polymers ABS 3501E Natural 1002 ESCR Extrusion Grade, Environmental Stress Crack Resistant
- ConocoPhillips Hydroclear® 10W-30 Super All Season and Super Motor Oil
- Entec Hypro™ PPC-GF40 Natural Impact Polypropylene, 40% Glass Reinforced
- Covestro Makrolon® KU1-1230* Polycarbonate
- NOVA Chemicals Novapol® TR-0535-UG Hexene MDPE Rotational Molding Resin (discontinued **)
- SABIC Innovative Plastics Ultem 2110N PEI
- Bulk Molding Compounds BMC T60-6009 Compression Grade Wear Resistant Molding Compound
Copyright © lookpolymers.com All Rights Reserved