Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 95.0 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C @Thickness 3.18 mm	203 °F @Thickness 0.125 in	Annealed; ASTM D648
PolyOne LubriOne™ AS-000/15T Acrylonitrile Butadiene Styrene (ABS) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F
Polycasa Acryl® G 77 Acrylic, Injection Molding Grade Injection molding grade for record player covers, optical fibers, display windows, logos, condiment containers, desk organizers.Data was collected by ISO methods.Quinn Manufacturing Group rebranded ..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C @Thickness 3.20 mm	203 °F @Thickness 0.126 in	ASTM D 648
SABIC Innovative Plastics Cycolac® INP564 ABS SABIC INP564 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	120°C/h; ISO 75/1
Polykemi AB POLYelast TPE 10012 R3 Thermoplastic Elastomer, PP/Elastomer, Mineral Reinforced Information provided by Polykemi AB
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	120°C/h; ISO 75/1
Polykemi AB POLYfill PPHC K2040H Polypropylene, Mineral Reinforced Information provided by Polykemi AB
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
PolyMirae Moplen RP340R Injection Molding Grade Polypropylene Moplen RP340R is the polypropylene random copolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen RP340R is a random copolymer particularly suitable for injecti..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C @Thickness 3.18 mm	203 °F @Thickness 0.125 in	Unannealed; ASTM D648
PolyOne Edgetek® XT X XT 1000 Natural Copolyester Edgetek™ XT high performance blends offer outstanding strength, durability and chemical resistance through the combination of Eastman Tritan™ copolyester with other various polymeric resins. Edget..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F
Polimeri Europa SINKRAL B733/E ABS, Impact & Heat Stabilized Grade (discontinued **) Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,EG,095-04-35-15 Very high impact resistant grade for sheet extrusion with good processability and high thermal sta..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C	203 Â°F	ASTM D648
Flint Hills P4G2Z-026 Homopolymer Polypropylene Homopolymer, UL certified, and FDA compliant.Features: Low water carryover.Applications: Extrusion: tape and strapping.Former Huntsman polypropylene products are now produced by Flint Hills Resource..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C	203 Â°F	ASTM D648
Lotte Chemical Titan TITANPROÂ® PD943 Polypropylene homopolymer The base resin meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520(a)(1)(i) and (c)1.1a. The adjuvants meet their respective FDA regulations and 21 CFR 1..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C	203 Â°F	ISO 75-1, -2
Lanxess DurethanÂ® TP 142-011 900116 Nylon 6 PA 6, non-reinforced, extrusion, blow molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C	203 Â°F
LATI Latistat 83-05 POM, Impact Modified Dissipative product based on Polyamide 12 (PA12), impact modified. Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indust..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C	203 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics XenoyÂ® HX6600HP PBT+PC (Europe-Africa-Middle East) Xenoy HX6600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C @Thickness 6.40 mm	203 Â°F @Thickness 0.252 in	ASTM D648
Samsung Cheil Industries InfinoÂ® GC-1015 PC/ABS, FR Information provided by Samsung Cheil Industries.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C @Thickness 6.40 mm	203 Â°F @Thickness 0.252 in	ASTM D648
Samsung Cheil Industries StarexÂ® GC-0770 H ABS/PET, Unreinforced Recycled Eco-friendly Post-Consumer recycled PET.Information provided by Samsung Cheil Industries.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
A. Schulman POLYFLAM™ RPP 1058 General Purpose Homopolymer Polypropylene (30% Fiberglass) DescriptionPolyflam® RPP 1058 is a general purpose homopolymer polypropylene flame retardant with a UL-V2 flammability rating and 105°C temperature index at 0.030 in.Information provided by A. Sch..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
Formosa Plastics Formolene® 6610A Impact Copolymer Polypropylene Impact Copolymer for Compounding and Injection Molded Applications Formolene® 6610A is a high impact copolymer of polypropylene designed for such injection applications as automotive compounding, l..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	120°C per hour; ISO 75-2
Total PPC 7642 Polypropylene, Heterophasic Copolymer ATOFINA Propylene 7642 is a nucleated and antistatic heterophasic copolymer. PPC 7642 is characterized by a very high stiffness.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	120°C per hour; ISO 75-2
Total PPH 9089 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 9089 is a very low molecular weight distribution homopolymer propylene, with anti gas-fading stabilization. ApplicationATOFINA Polypropylene PPH 9089 is intended for the ex..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	120°C per hour; ISO 75-2
Total PPH 9099 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 9099 is a very narrow molecular weight distribution homopolymer polypropylene, with anti gas-fading stabilization. ApplicationATOFINA Polypropylene PPH 9099 is intended for..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
A. Schulman POLYFORT™ FPP 1245 CaCO3 Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1245 is a 20% CAC03 filled copolymer polypropylene product. Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
A. Schulman PP 1632-01 Polypropylene Random Copolymer DescriptionPolypropylene PP 1632-01 is a polypropylene random copolymer produced utilizing unique catalyst and processing technology. It was designed for injection molding and stretch blow molding ..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F
Covestro Bayblend® FR 3001 Polycarbonate + ABS Blend Key Features:Flame retarding agentUnfilledFlame retardantSuitable processing methods:Injection moldingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialScience was separat..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ISO 75-1/-2
Covestro Bayblend® FR 3008 Polycarbonate + ABS, Flame Retardant Grade Injection molding gradeHDT/A = 85 °CVicat/B 120 temperature = 103 °CUL-listing 94 V-0 (1.5 mm)improved chemical and hydrolysis resistance antimony-, chlorine- and bromine-free flame retardant..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
LATI LASTIROL TR G/10-V1 ES 10% Glass Fiber Polystyrene (PS) Structural Foam Resin (UL94 V-1) (discontinued * Description: Lastirol thermoplastics are polystyrene (PS) products. The Lastirols feature excellent dimensional stability, good flowability, and can be molded without any particular problem. Glass f..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F
BASF Novolen® 1148 TC Polypropylene Nucleated grade with antistatic agent for injection molded parts.Data was collected by ISO methods and provided by BASF.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C @Thickness 3.20 mm	203 °F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics LNP Stat-kon MX01767C PP LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB..