Covestro Bayblend® FR 3001 Polycarbonate + ABS Blend

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	Covestro
Trade Name	Bayblend®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Covestro Bayblend® FR 3001 Polycarbonate + ABS Blend.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Features:Flame retarding agentUnfilledFlame retardantSuitable processing methods:Injection moldingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in³
Water Absorption	0.40 %	0.40 %
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C/50% R.H.
Melt Flow	25 g/10 min @Load 5.00 kg, Temperature 240 °C	25 g/10 min @Load 11.0 lb, Temperature 464 °F	cm³/10 min.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	60.0 MPa	8700 psi
Elongation at Break	30 %	30 %	Nominal
Elongation at Yield	4.0 %	4.0 %
Tensile Modulus	2.70 GPa	392 ksi

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	78.0 µm/m-°C @Temperature 20.0 °C	43.3 µin/in-°F @Temperature 68.0 °F
CTE, linear, Transverse to Flow	80.0 µm/m-°C @Temperature 20.0 °C	44.4 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F
Deflection Temperature at 1.8 MPa (264 psi)	85.0 °C	185 °F
Vicat Softening Point	101 °C	214 °F	50°C/h 50N
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	UL Recognized
	5VA @Thickness 3.00 mm	5VA @Thickness 0.118 in	UL Recognized

Electrical Properties	Metric	English
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm
Dielectric Constant	3.1 @Frequency 100 Hz	3.1 @Frequency 100 Hz
	3.1 @Frequency 1e+6 Hz	3.1 @Frequency 1e+6 Hz
Dielectric Strength	30.0 kV/mm	762 kV/in
Dissipation Factor	0.0050 @Frequency 100 Hz	0.0050 @Frequency 100 Hz
	0.0070 @Frequency 1e+6 Hz	0.0070 @Frequency 1e+6 Hz
Comparative Tracking Index	300 V	300 V

Processing Properties	Metric	English	Comments
Melt Temperature	240 °C	464 °F	Injection Molding
Mold Temperature	80.0 °C	176 °F	Injection Molding
Injection Velocity	240 mm/sec	9.45 in/sec