- Polymer Property : CTE, linear = 13.9 µm/m-°C
Polymer Property : CTE, linear = 13.9 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.9 µm/m-°C @Temperature 0.000 - 100 °C |
7.72 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Kennametal Stellite Stellite® 6 PM cast Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 0.000 - 100 °C |
7.72 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 0.000 - 100 °C |
7.72 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.7 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 0.000 - 100 °C |
7.72 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 20.0 - 700.0 °C |
7.72 µin/in-°F @Temperature 68.0 - 1292 °F |
|
| International Mold Steel DH2F Pre-Hardened H13-Type Mold Steel Description: DH2F is one of the best machining pre-hardened H13-type steels available.Unique Characteristics: 38-42 HRc hardness.Through hardened for exceptional dimensional stability.Cuts mold maki.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 20.0 - 500 °C |
7.72 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Industeel CREUSABRO® 4000 High Wear Resistant Steel Description: CREUSABRO® 4000 is a high wear resistant steel, offering a 30 % extra in service life compared to a conventional 400 HB water quenched. Improved properties of CREUSABRO® 4000 resu.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 0.000 - 100 °C |
7.72 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 25.0 - 900 °C |
7.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes Hastelloy® B-3® alloy, 10% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 25.0 - 900 °C |
7.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 25.0 - 900 °C |
7.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes Hastelloy® B-3® alloy, 30% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, 10% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, 60% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, GMAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 10% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 15% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 30% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 40% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 5% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 50% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC. This produces ASTM grain size 5.5. Other property values are ty.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1200°F (650°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC + Aged 1200°F (650°C)/100h/AC. This produces ASTM grain siz.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 20.0 - 538 °C |
7.70 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| Crucible Steel CSM® 6 Tool Steel, AISI A6 CSM 6 is an air hardening tool steel offering moderate wear resistance and toughness. It may be hardened from a low hardening temperature for easy heat treatment.Information provided by Crucible Ind.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 20.0 - 93.0 °C |
7.72 µin/in-°F @Temperature 68.0 - 199 °F |
|
| ATI Allegheny Ludlum AL 400™ Nickel-Base Alloy, Hot Rolled Plate, UNS N04400 Moderately to faintly magnetic at room temperature. Allegheny Ludlum AL 400 alloy is a ductile nickel-copper alloy with resistance to a variety of corrosive conditions. The alloy is most frequentl.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 25.0 - 900 °C |
7.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes Hastelloy® B-3® alloy, heat treated at 1065°C, rapid quenched The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ea.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 20.0 - 315 °C |
7.72 µin/in-°F @Temperature 68.0 - 599 °F |
|
| ATI Allegheny Ludlum Altemp® 718 Nickel-Base Superalloy, Solution Treated plus Precipitation Heat Treated, UNS N07718 Allegheny Ludlum Altemp 718 alloy is an austenitic nickel-base superalloy which is used in applications requiring high strength to approximately 760 degrees Celsius and oxidation resistance to appro.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, 0% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, all-weld metal, GTAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||