Kennametal Stellite Stellite® 6 PM cast

Category Metal , Nonferrous Metal , Cobalt Alloy , Superalloy
Manufacturer Kennametal Stellite
Trade Name Stellite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kennametal Stellite Stellite® 6 PM cast.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wear parts. Data provide by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.
Physical Properties Metric English Comments
Density 8.20 g/cc
0.296 lb/in³
P/M (98%)
8.38 g/cc
0.303 lb/in³
theoretical
Mechanical Properties Metric English Comments
Hardness, Brinell 364
364
Converted from Rockwell C hardness.
224

@Temperature 760 °C
 224

@Temperature 1400 °F
 Converted from Rockwell C hardness
312

@Temperature 649 °C
 312

@Temperature 1200 °F
 Converted from Rockwell C hardness
345

@Temperature 538 °C
 345

@Temperature 1000 °F
 Converted from Rockwell C hardness
Hardness, Knoop 436
436
Converted from Rockwell C hardness.
262

@Temperature 760 °C
 262

@Temperature 1400 °F
 Converted from Rockwell C hardness
372

@Temperature 649 °C
 372

@Temperature 1200 °F
 Converted from Rockwell C hardness
413

@Temperature 538 °C
 413

@Temperature 1000 °F
 Converted from Rockwell C hardness
Hardness, Rockwell A 70
70
Converted from Rockwell C hardness.
60

@Temperature 760 °C
 60

@Temperature 1400 °F
 Converted from Rockwell C hardness
67

@Temperature 649 °C
 67

@Temperature 1200 °F
 Converted from Rockwell C hardness
69

@Temperature 538 °C
 69

@Temperature 1000 °F
 Converted from Rockwell C hardness
Hardness, Rockwell C 40
40
19

@Temperature 760 °C
 19

@Temperature 1400 °F
34

@Temperature 649 °C
 34

@Temperature 1200 °F
38

@Temperature 538 °C
 38

@Temperature 1000 °F
Hardness, Vickers 383
383
Converted from Rockwell C hardness.
230

@Temperature 760 °C
 230

@Temperature 1400 °F
 Converted from Rockwell C hardness
326

@Temperature 649 °C
 326

@Temperature 1200 °F
 Converted from Rockwell C hardness
362

@Temperature 538 °C
 362

@Temperature 1000 °F
 Converted from Rockwell C hardness
Tensile Strength, Ultimate 911 MPa
132000 psi
552 MPa

@Temperature 760 °C
 80100 psi

@Temperature 1400 °F
676 MPa

@Temperature 649 °C
 98000 psi

@Temperature 1200 °F
759 MPa

@Temperature 538 °C
 110000 psi

@Temperature 1000 °F
Elongation at Break <= 1.0 %
<= 1.0 %
in 25.4 mm
1.0 %

@Temperature 538 °C
 1.0 %

@Temperature 1000 °F
 in 25.4 mm
2.0 %

@Temperature 649 °C
 2.0 %

@Temperature 1200 °F
 in 25.4 mm
5.0 %

@Temperature 760 °C
 5.0 %

@Temperature 1400 °F
 in 25.4 mm
Thermal Properties Metric English Comments
CTE, linear 13.9 µm/m-°C

@Temperature 0.000 - 100 °C
 7.72 µin/in-°F

@Temperature 32.0 - 212 °F
14.1 µm/m-°C

@Temperature 0.000 - 200 °C
 7.83 µin/in-°F

@Temperature 32.0 - 392 °F
14.5 µm/m-°C

@Temperature 0.000 - 300 °C
 8.06 µin/in-°F

@Temperature 32.0 - 572 °F
14.7 µm/m-°C

@Temperature 0.000 - 400 °C
 8.17 µin/in-°F

@Temperature 32.0 - 752 °F
15.0 µm/m-°C

@Temperature 0.000 - 500 °C
 8.33 µin/in-°F

@Temperature 32.0 - 932 °F
15.3 µm/m-°C

@Temperature 0.000 - 600 °C
 8.50 µin/in-°F

@Temperature 32.0 - 1110 °F
15.8 µm/m-°C

@Temperature 0.000 - 700 °C
 8.78 µin/in-°F

@Temperature 32.0 - 1290 °F
16.3 µm/m-°C

@Temperature 0.000 - 800 °C
 9.06 µin/in-°F

@Temperature 32.0 - 1470 °F
16.9 µm/m-°C

@Temperature 0.000 - 900 °C
 9.39 µin/in-°F

@Temperature 32.0 - 1650 °F
17.4 µm/m-°C

@Temperature 0.000 - 1000 °C
 9.67 µin/in-°F

@Temperature 32.0 - 1830 °F
Melting Point 1260 - 1357 °C
2300 - 2475 °F
Solidus 1260 °C
2300 °F
Liquidus 1357 °C
2475 °F
Component Elements Properties Metric English Comments
Boron, B <= 1.0 %
<= 1.0 %
Carbon, C 1.2 %
1.2 %
Chromium, Cr 29 %
29 %
Cobalt, Co 52.3 %
52.3 %
As remainder
Iron, Fe <= 3.0 %
<= 3.0 %
Manganese, Mn 1.0 %
1.0 %
Molybdenum, Mo <= 1.5 %
<= 1.5 %
Nickel, Ni <= 3.0 %
<= 3.0 %
Other <= 2.0 %
<= 2.0 %
Silicon, Si <= 1.5 %
<= 1.5 %
Tungsten, W 4.5 %
4.5 %
Electrical Properties Metric English Comments
Magnetic Permeability <= 1.20

@Temperature 22.0 °C
 <= 1.20

@Temperature 71.6 °F
 200 Oersted