- Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 30% Cold Work
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 30% Cold Work
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCONEL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 30% Cold Work.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of this alloy.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.44 g/cc | 0.305 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 973.5 MPa | 141200 psi | |
| Tensile Strength, Yield | 527 MPa @Strain 0.200 % |
76400 psi @Strain 0.200 % |
|
| Elongation at Break | 42 % | 42 % | |
| Modulus of Elasticity | 208 GPa | 30200 ksi | |
| Poissons Ratio | 0.28 | 0.28 | |
| Shear Modulus | 81.4 GPa | 11800 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 100 °C |
7.11 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| 13.3 µm/m-°C @Temperature 21.0 - 300 °C |
7.39 µin/in-°F @Temperature 69.8 - 572 °F |
Mean | |
| 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean | |
| 14.9 µm/m-°C @Temperature 21.0 - 700 °C |
8.28 µin/in-°F @Temperature 69.8 - 1290 °F |
Mean | |
| Specific Heat Capacity | 0.410 J/g-°C | 0.0980 BTU/lb-°F | |
| Thermal Conductivity | 9.70 W/m-K | 67.3 BTU-in/hr-ft²-°F | |
| Melting Point | 1290 - 1350 °C | 2350 - 2460 °F | |
| Solidus | 1290 °C | 2350 °F | |
| Liquidus | 1350 °C | 2460 °F | |
| Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | <= 0.40 % | <= 0.40 % | |
| Carbon, C | <= 0.030 % | <= 0.030 % | |
| Chromium, Cr | 20 - 23 % | 20 - 23 % | |
| Cobalt, Co | <= 1.0 % | <= 1.0 % | |
| Iron, Fe | <= 5.0 % | <= 5.0 % | |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Molybdenum, Mo | 8.0 - 10 % | 8.0 - 10 % | |
| Nickel, Ni | >= 58 % | >= 58 % | |
| Niobium, Nb (Columbium, Cb) | 3.15 - 4.15 % | 3.15 - 4.15 % | Includes Ta |
| Nitrogen, N | <= 0.020 % | <= 0.020 % | |
| Phosphorous, P | <= 0.015 % | <= 0.015 % | |
| Silicon, Si | <= 0.020 % | <= 0.020 % | |
| Sulfur, S | <= 0.015 % | <= 0.015 % | |
| Titanium, Ti | <= 0.40 % | <= 0.40 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000132 ohm-cm | 0.000132 ohm-cm | |
| Magnetic Permeability | 1.0006 | 1.0006 | at 200 Oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® IR2040 PC (Europe-Africa-Middle East)
- PolyOne Edgetek® 5209 Black 30 A 1 Acetal (POM) Copolymer
- Lord Adhesives 7412 Single Component, Moisture Cure, 100% Solids Urethane Adhesive
- Samsung Cheil Industries Starex® VS-0826 ABS, Unreinforced FR
- EMS-Grivory Grivory® TR XE 4139 black 9231 PA*
- 3M 7028FL Screen Printable Polyester Performance LabelProducts
- 3M Pronto™ CA-40 Instant Adhesive
- ATI Allegheny Ludlum AL 800™ Nickel-Base Alloy, UNS N08800
- A. Schulman POLYBLAK™ 4479-01A Black Color Concentrate, 50% Carbon Black Based In Polyethylene
Copyright © lookpolymers.com All Rights Reserved